摩擦辅助喷射电沉积制备纳米晶光亮镍

华南理工大学学报(自然科学版) ›› 2011, Vol. 39 ›› Issue (11): 92-97.

摩擦辅助喷射电沉积制备纳米晶光亮镍

朱军^1,2田宗军^1,2刘志东^1,2沈理达^1,2黄因慧^1,2王桂峰²

1．南京航空航天大学江苏省精密与微细制造技术重点实验室，江苏南京 210016; 2．南京航空航天大学机电学院，江苏南京 210016

收稿日期:2011-06-01 修回日期:2011-07-14 出版日期:2011-11-25 发布日期:2011-10-03
通信作者: 朱军(1983-) ，男，博士生，主要从事特种加工新技术研究． E-mail:hygf2008@ sina.com
作者简介:朱军(1983-) ，男，博士生，主要从事特种加工新技术研究．
基金资助:
江苏省自然科学基金资助项目( BK2009375)

Preparation of Bright Nano-Crystalline Nickel via Friction-Aided Jet Electrodeposition

Zhu Jun^1,2Tian Zong-jun^1,2Liu Zhi-dong^1,2Shen Li-da^1,2Huang Yin-hui^1,2Wang Gui-feng²

1. Jiangsu Key Laboratory of Precision and Micro-Manufacturing Technology,Nanjing University of Aeronautics and Astronautics,Nanjing 210016,Jiangsu,China; 2. College of Mechanical and Electrical Engineering,Nanjing University of Aeronautics and Astronautics,Nanjing 210016,Jiangsu,China

Received:2011-06-01 Revised:2011-07-14 Online:2011-11-25 Published:2011-10-03
Contact: 朱军(1983-) ，男，博士生，主要从事特种加工新技术研究． E-mail:hygf2008@ sina.com
About author:朱军(1983-) ，男，博士生，主要从事特种加工新技术研究．
Supported by:
江苏省自然科学基金资助项目( BK2009375)

摘要/Abstract

摘要： 针对传统喷射电沉积技术的不足，提出一种新型的摩擦辅助喷射电沉积技术．分别使用该技术和传统喷射电沉积技术制备了一组镍沉积层，利用XRD、TEM 分析了沉积层的组织结构，用显微硬度计测试了沉积层的表面显微形貌和显微硬度，并用振动样品磁强计测试了沉积层的磁性能．结果表明: 采用该技术可以制备出表面平整光亮的电沉积层，所制备的镍沉积层具有纳米晶微观结构，平均晶粒尺寸约为10 nm，远小于传统喷射电沉积技术制得的沉积层的平均晶粒尺寸; 摩擦辅助作用细化了晶粒，改善了沉积层的组织结构，提高了结构层的硬度，沉积层磁性能也有很大改变．

关键词: 喷射电沉积, 摩擦, 纳米晶, 镍, 显微形貌, 磁性能

Abstract:

In order to overcome the disadvantages of the traditional jet electrodeposition,a novel friction-aided technology was proposed. To make a comparison,nickel deposition layers were prepared by using the proposed and the traditional technologies,respectively. Afterwards,the microstructure,surface morphology,microhardness and magnetic properties of the layers were investigated by means of XRD,TEM,microhardness test and vibrating-sample magnetic strength test. The results show that the friction-aided technology helps to prepare electrodeposition layer with smooth and bright surface and well-organized structure,that the deposited nickel layers are all in nano-crystalline microstructure whose average size ( about 10 nm) is far less than that prepared by the traditional jet electrodeposition technology,and that the friction helps to refine the grains,improve the microstructure,increase the hardness of the deposited layer,and greatly change the magnetic properties of the deposited layers.

Key words: jet electrodeposition, friction, nano-crystalline, nickel, micro-appearance, magnetic property

中图分类号:

TG662
TQ153

朱军田宗军刘志东沈理达黄因慧王桂峰. 摩擦辅助喷射电沉积制备纳米晶光亮镍[J]. 华南理工大学学报(自然科学版), 2011, 39(11): 92-97.

Zhu Jun Tian Zong-jun Liu Zhi-dong Shen Li-da Huang Yin-hui Wang Gui-feng. Preparation of Bright Nano-Crystalline Nickel via Friction-Aided Jet Electrodeposition[J]. Journal of South China University of Technology(Natural Science Edition), 2011, 39(11): 92-97.

[1]	张跃明, 李天宇, 纪姝婷. 摆线针轮减速机参数对效率的影响与参数优化[J]. 华南理工大学学报(自然科学版), 2024, 52(4): 77-87.
[2]	叶伯生, 李思澳, 谭帅, 等. 基于速度控制的机器人轨迹摩擦补偿研究[J]. 华南理工大学学报(自然科学版), 2024, 52(4): 51-58.
[3]	黄惠华, 唐璐, 刘钰姗, 等. 菠萝皮渣纤维素纳米晶的制备及其在Pickering乳液中的环境稳定性[J]. 华南理工大学学报(自然科学版), 2022, 50(8): 1-11.
[4]	梁瑛娜, 高建新, 高殿荣. 仿生非光滑表面滑靴副水压轴向柱塞泵摩擦磨损及效率试验研究[J]. 华南理工大学学报(自然科学版), 2022, 50(6): 145-154.
[5]	王延忠, 窦德龙, 张震, 等. 多锥构型摩擦副同步过程影响因素分析[J]. 华南理工大学学报(自然科学版), 2022, 50(2): 58-66,83.
[6]	李刚, 李锋, 丁孺琦, 等. 基于关节力矩补偿的液压机械臂末端力软测量[J]. 华南理工大学学报(自然科学版), 2022, 50(10): 140-152.
[7]	姜继海杜博然张健. 轴向柱塞泵液－磁复合支撑的应用前景及技术展望[J]. 华南理工大学学报(自然科学版), 2021, 49(2): 88-98,109.
[8]	侯亮, 赖伟群, 崔凯, 等. 轴向柱塞马达平面配流副油膜润滑特性建模及分析[J]. 华南理工大学学报(自然科学版), 2021, 49(2): 99-109,139.
[9]	王延忠, 徐梓淳, 马涛, 等. 修形人字齿轮的润滑及摩擦特性分析[J]. 华南理工大学学报（自然科学版）, 2021, 49(1): 93-102.
[10]	梁云张日盈张春辉. 湿式纸基摩擦材料的压缩回弹性能[J]. 华南理工大学学报（自然科学版）, 2020, 48(8): 82-90.
[11]	张伟, 李淳潮, 李志远, 等. 新型系泊机构气动控制分支建模及摩擦力补偿试验研究[J]. 华南理工大学学报(自然科学版), 2020, 48(2): 122-128.
[12]	耿魁伟徐志平李徐. 基于 MoS₂ /Graphene 复合材料的摩擦纳米发电机[J]. 华南理工大学学报(自然科学版), 2020, 48(10): 113-119,128.
[13]	段志鹏宁晓茹苏良彬马浩. 矩形微通道流动入口段的阻力特性分析[J]. 华南理工大学学报(自然科学版), 2019, 47(9): 18-23.
[14]	王安麟于永强李晓田王楚昕. 可用于塑性材料的离散单元滞回力矩滚动阻力模型[J]. 华南理工大学学报(自然科学版), 2019, 47(5): 56-62，72.
[15]	陆龙生方何正子谢颖熙孙佳伟万珍平 . 碳纤维锻造复合材料的摩擦行为 [J]. 华南理工大学学报（自然科学版）, 2019, 47(1): 7-13.