Carbonation Properties and Pore Characteristics of Different Interfaces in Recycled Lump/Aggregate Concrete

doi:10.12141/j.issn.1000-565X.220637

Abstract

Abstract:

Scientifically grasping the durability performance of the recycled lump/aggregate concrete (RLAC) is of great significance for promoting the engineering application of this type of concrete. In this paper, to reveal the carbonation properties of the stone-mortar interface and the new mortar-old mortar interface in RLAC, rapid carbonation tests of these two kinds of interfaces and the mortar matrix were carried out, and the porosity of the new mortar-old mortar interfacial transition zone was investigated through backscatter electron images. The results show that the carbonization depth of the interfacial transition zone is greater than that of the mortar matrix, and the closer to the interface, the greater the degree of carbonization, showing an obvious two-dimension carbonization superposition phenomenon. The interface carbonization depths of the stone-mortar specimens vary from 26 to 46 mm, while those of the mortar-mortar specimens are only 7~15 mm. As compared with the new mortar-old mortar interface, the carbonization depth of the stone-mortar interface is much greater, indicating the latter interface having a weaker carbonization resistance. The water-to-cement ratio of the new mortar has a great influence on the carbonation performance of the new mortar-old mortar interface, and the related reduction in carbonization depth is between 15% and 52%, while the water-to-cement ratio of the old mortar has no obvious effect on the carbonation performance of such interface. When the water-to-cement ratio of the new mortar is fixed, the porosity of the new mortar-old mortar interface is almost unchanged with the water-to-cement ratio of the old mortar. However, when the water-to-cement ratio of the old mortar is fixed, the porosity of such interface decreases greatly with the reducing of the water-to-cement ratio of the new mortar. There thus comes to the conclusion that, in practical engineering, the carbonation performance of the new mortar-old mortar interface can be effectively improved by controlling the water-to-cement ratio of the new mortar.

Key words: recycled lump/aggregate concrete, interface, carbonation property, pore characteristic

CLC Number:

TU502

WU Bo, HUANG Tingting. Carbonation Properties and Pore Characteristics of Different Interfaces in Recycled Lump/Aggregate Concrete[J]. Journal of South China University of Technology(Natural Science Edition), 2023, 51(7): 52-60.

Figures/Tables 10

Fig.1

Table 1

Table 2

Fig.2

Table 3

Fig.3

Fig.4

Fig.5

Fig.6

Fig.7

References 34

1	EVANGELISTA L， DE BRITO J ．Concrete with fine recycled aggregates：a review［J］．European Journal of Environmental and Civil Engineering，2014，18（2）：129-172．
2	KISKU N， JOSHI H， ANSARI M，et al ．A critical review and assessment for usage of recycled aggregate as sustainable construction material［J］．Construction and Building Materials，2017，131（30）：721-740．
3	CORINALDESI V ．Mechanical and elastic behaviour of concretes made of recycled-concrete coarse aggregates［J］．Construction and Building Materials，2010，24（9）：1616-1620．
4	WANG Z， WANG L， CUI Z，et al ．Effect of recycled coarse aggregate on concrete compressive strength［J］．Transactions of Tianjin University，2011，17（3）：229-234．
5	KOU S， ZHAN B， POON C ．Feasibility study of using recycled fresh concrete waste as coarse aggregates in concrete［J］．Construction and Building Materials，2012，28（1）：549-556．
6	ANDREU G， MIREN E ．Experimental analysis of properties of high performance recycled aggregate concrete［J］．Construction and Building Materials，2014，52（15）：227-235．
7	KOU S， POON C ．Effect of the quality of parent concrete on the properties of high performance recycled aggregate concrete［J］．Construction and Building Materials，2015，77（15）：501-508．
8	PEDRO D， DE BRITO J， EVANGELISTA L ．Structural concrete with simultaneous incorporation of fine and coarse recycled concrete aggregates：mechanical，durability and long-term properties［J］．Construction and Building Materials，2017，154（15）：294-309．
9	LONG L， POON C， XIAO J，et al ．Effect of carbonated recycled coarse aggregate on the dynamic compressive behavior of recycled aggregate concrete［J］．Construction and Building Materials，2017，151（1）：52-62．
10	邸芃，付翠萍．废弃混凝土破碎工艺及再生骨料的利用研究［C］∥2014中国环境科学学会学术年会论文集．成都：中国环境科学学会，2014：5639-5643．
11	吴波，刘琼祥，刘伟，等．钢管再生混合构件初探［J］．工程抗震与加固改造，2008，30（4）：120-124．
	WU Bo， LIU Qiong-xiang， LIU Wei，et al ．Preliminary study on steel recycled mixed members［J］．Earthquake Resistance and Reinforcement of Engineering，2008，30（4）：120-124．
12	严华．再生混合混凝土及薄壁圆钢管再生混合短柱的轴压徐变性能试验研究［D］．广州：华南理工大学，2014．
13	余勇．再生块体混凝土常温及高温后力学性能研究［D］．广州：华南理工大学，2019．
14	金和卯．再生块体混凝土的疲劳性能研究［D］．广州：华南理工大学，2020．
15	WU B， LI Z ．Mechanical properties of compound concrete containing demolished concrete lumps after freeze-thaw cycles［J］．Construction and Building Materials，2017，155（30）：187-199．
16	WU B， YAN J ．Influences of size and shape of demolished concrete lumps on compressive behavior of compound concrete［J］．Construction and Building Materials，2021，269（1）：121317．
17	JIAN S， WU B ．Compressive behavior of compound concrete containing demolished concrete lumps and recycled aggregate concrete［J］．Construction and Building Materials，2021，272（22）：121624．
18	LIN L， WU B ．Water permeability behavior of recycled lump/aggregate concrete［J］．Construction and Building Materials，2022，323（14）：126508．
19	SILVA R V， NEVES R， DE BRITO J ．Carbonation behaviour of recycled aggregate concrete［J］．Cement & Concrete Composites，2015，62：22-32．
20	申健，牛荻涛，王艳，等．再生混凝土耐久性能研究进展［J］．材料导报，2016，30（3）：89-94，100．
	SHEN Jian， NIU Ditao， WANG Yan，et al ．Research progress on durability of recycled concrete［J］．Materials Reports，2016，30（3）：89-94，100．
21	王吉云．再生骨料碳化处理对再生混凝土渗透性和界面的影响［D］．长沙：湖南大学，2017．
22	PAPADAKIS V G， VAYENAS C G， FARDIS M N ．Experimental investigation and mathematical modeling of the concrete carbonation problem［J］．Chemical Engineering Science，1991，46（5/6）：1333-1338．
23	牛海成，范玉辉，张向冈，等．再生混凝土抗碳化性能试验研究［J］．硅酸盐通报，2018，37（1）：59-66．
	NIU Hai-cheng， FAN Yu-hui， ZHANG Xiang-gang，et al ．Experimental study on carbonation behaviour of recycled concrete［J］．Bulletin of the Chinese Ceramic Society，2018，37（1）：59-66．
24	沈奇真．碳化与荷载耦合作用下水泥基材料微结构演变与预测模型［D］．南京：东南大学，2018．
25	MI R， PAN G， SHEN Q ．Carbonation modelling for cement-based materials considering influences of aggregate and interfacial transition zone［J］．Construction and Building Materials，2019，229（30）：116925．
26	GARBOCZI E J， BENTZ D P ．Multiscale analytical/numerical theory of the diffusivity of concrete［J］．Advanced Cement Based Materials，1998，8（2）：77-88．
27	普通混凝土长期性能和耐久性能试验方法标准：［S］．
28	建筑砂浆基本性能试验方法标准：［S］．
29	STUTZMAN P E， CLIFTON J R ．Specimen preparation for scanning electron microscopy［C］∥Proceedings of the Twenty-First International Conference on Cement Microscopy．Nevada：National Institute of Standards and Technology，1999：10-22．
30	KJELLSEN K O， MONSY A， ISACHSEN K，et al ．Preparation of flat-polished specimens for SEM-backscattered electron imaging and X-ray microanalysis-importance of epoxy impregnation［J］．Cement and Concrete Research，2003，33（4）：611-616．
31	WONG H S， HEAD M K， BUENFELD N R ．Pore segmentation of cement-based materials from backscattered electron images［J］．Cement and Concrete Research，2006，36（6）：1083-1090．
32	JIANG Z， HUANG Q， XI Y，et al ．Experimental study of diffusivity of the interfacial transition zone between cement paste and aggregate［J］．Journal of Materials in Civil Engineering，2016，28（10）：04016109/1-8．
33	WU K， SHI H， XU L，et al ．Microstructural characterization of ITZ in blended cement concretes and its relation to transport properties［J］．Cement and Concrete Research，2016，79：243-256．
34	DIAMOND S， HUANG J ．The ITZ in concrete-a different view based on image analysis and SEM observations［J］．Cement and Concrete Composites，2001，23（2/3）：179-188．

试件类型	组别	水灰比
试件类型	组别	先浇砂浆	后浇砂浆
砂浆试件	1	—	0.3
	2	—	0.4
	3	—	0.5
石片-砂浆试件	4	—	0.3
	5	—	0.4
	6	—	0.5
砂浆-砂浆试件	7	0.3	0.3
	8		0.4
	9		0.5
	10	0.4	0.3
	11		0.4
	12		0.5
	13	0.5	0.3
	14		0.4
	15		0.5

水灰比	添加量/（kg·m^-3）
水灰比	水	水泥	细骨料	粗骨料	减水剂
0.3	215	717	514	954	1.36
0.4	215	538	577	1 071	0.70
0.5	215	430	614	1 141	0.40

龄期/d	不同水灰比下的抗压强度/MPa
龄期/d	0.5	0.4	0.3
28	50.4	64.6	82.4
56	49.8	61.0	86.2

[1]	LU Hongyao, XU Yude. Evolution of Interface Performance of Longitudinal Ballastless Track Under Temperature Load After Embedded Steel Bars [J]. Journal of South China University of Technology(Natural Science Edition), 2023, 51(8): 21-31.
[2]	DENG Kailing, WANG Duanyi, FANG Qiuping. Fracture Energy Test Method and Influencing Factors of Asphalt-Aggregate Interface [J]. Journal of South China University of Technology(Natural Science Edition), 2023, 51(8): 12-20.
[3]	WU Bo, CHEN Zhaonan, WANG Hui. Creep Behavior of Reinforced and Unreinforced Recycled Lump/Aggregate Concrete [J]. Journal of South China University of Technology(Natural Science Edition), 2022, 50(7): 35-42.
[4]	YIN Yushi FAN Yingfang GUO Xinyan. Effects of Roughness on Interfacial Bonding Properties Between Concrete and FRP [J]. Journal of South China University of Technology (Natural Science Edition), 2019, 47(5): 130-138.
[5]	TANG Zhengqiang ZHOU Dongdong JIA Tong ZHANG Chuanwei . Analysis of the Mechanical Properties of Head /Disk Interface in Air-Helium Gas Mixtures [J]. Journal of South China University of Technology (Natural Science Edition), 2019, 47(3): 44-52.
[6]	CHENG Hao WANG Xuan ZHANG Jiasheng WANG Qiyun. Effects of Ｒoughness on Cyclic Shear Behavior of Ｒed Clay-Concrete Interface [J]. Journal of South China University of Technology (Natural Science Edition), 2018, 46(4): 146-152.
[7]	LI Jing CHEN Xuyang LEI Rubai ZHANG Ding FAN Chunlei. Research on Thermal Performance Of Bi-In-Sn-Sb Quaternary Alloy Interface Materials [J]. Journal of South China University of Technology (Natural Science Edition), 2018, 46(11): 39-46.
[8]	ZHAN Jia-ming YAO Xiao-hu LI Wang-hui. A Probe into Mechanical Properties of Graphene/ SiC Composites Based on Molecular Dynamics [J]. Journal of South China University of Technology (Natural Science Edition), 2017, 45(5): 135-140.
[9]	CAI Min-xi YAO Ruo-he. Effects of Active Layer Thickness of Dual-Gate Amorphous InGaZnO Thin Film Transistors on Their Electrical Characteristics [J]. Journal of South China University of Technology (Natural Science Edition), 2016, 44(9): 61-66,72.
[10]	XIAO Min-min. Mixture Composition Design and Interface Properties of Asphalt Plug Expansion Joint [J]. Journal of South China University of Technology (Natural Science Edition), 2016, 44(8): 106-113.
[11]	DAI Gong-lian SU Miao . Numerical Stimulation of Interface Delamination Failure for Prefabricated Slab Ballastless Track [J]. Journal of South China University of Technology (Natural Science Edition), 2016, 44(7): 102-107,122.
[12]	HONG Lei DUO Run-min WANG Su-yan. Influence of Bond Length on Bonded Interface Performance of CFRP-C60 Concrete [J]. Journal of South China University of Technology (Natural Science Edition), 2016, 44(2): 14-19.
[13]	LONG Yao ZHANG Jia-sheng CHEN Jun-hua. Shear Characteristics of Structure Interface and Its Strain-Softening and Hardening Damage Model [J]. Journal of South China University of Technology (Natural Science Edition), 2016, 44(12): 128-134.
[14]	LI Jing CHEN Hao YIN Yao-bao. Oil Characteristic Analysis of Piston-Cylinder Interface in Axial Piston Pump with Radial Micro-Motion [J]. Journal of South China University of Technology (Natural Science Edition), 2016, 44(10): 30-35,42.
[15]	Wu Guo- guang Liu Gui- xiong Zhou Song- bin. Modeling and Dynamic Performance Evaluation of WTIM Based on Petri Nets [J]. Journal of South China University of Technology (Natural Science Edition), 2013, 41(9): 107-112.