Journal of South China University of Technology (Natural Science Edition) ›› 2014, Vol. 42 ›› Issue (9): 12-17.doi: 10.3969/j.issn.1000-565X.2014.09.003

• Mechanical Engineering • Previous Articles     Next Articles

Crack Initiation and Propagation Laws of Graphite Specimen Subjected to Edge- Indentation

Zhang Shi- wei Wan Zhen- ping Ou Yuan- xian Xu Pei- jie Tang Yong   

  1. School of Mechanical and Automotive Engineering,South China University of Technology,Guangzhou 510640,Guangdong,China
  • Received:2014-04-22 Revised:2014-06-25 Online:2014-09-25 Published:2014-08-01
  • Contact: 万珍平(1971-)，男，教授，博士生导师，主要从事现代加工理论与技术研究． E-mail:zhpwan@scut.edu.cn
  • About author:张仕伟(1988-)，男，博士生，主要从事现代加工理论与技术研究．E-mail:190361407@qq．com
  • Supported by:

     国家自然科学基金资助项目(51075155);广州市科技计划项目(2013J4300012)

PDF

643

Abstract:

In order to reveal the cutting process of graphite materials and the forming mechanism of machined sur-faces,the crack initiation and propagation laws of a graphite specimen subjected to edge- indentation are investigated.The results show that (1) cracks initiate suddenly and propagate rapidly when the indentation loading increases to acritical value; (2) initial cracks spread toward the inside of specimens,and then propagate toward the indentationsurface gradually and reach the indentation surface finally,which occurs along an arc- shaped propagation path; and(3) as the interior angle of indenter and the edge- indentation thickness increase,the cracks spread farther towardthe inside of specimens and the depth and width of concavities forming on the specimen surface become greater.Inaddition,cutting experiments indicate that the crack initiation and propagation laws of the graphite specimen sub-jected to edge- indentation can be used to describe the material removal and the machined surface formation.

Key words: graphite cutting, edge- indentation, crack initiation, crack propagation

CLC Number: