四元共聚热塑性聚酰亚胺的合成与表征

曹贤武韦创何光建文江维

华南理工大学广东省高分子先进制造技术及装备重点实验室∥聚合物新型成型装备国家工程研究中心//聚合物加工工程教育部重点实验室，广东广州 510640

收稿日期:2019-10-17 修回日期:2019-12-19 出版日期:2020-04-25 发布日期:2020-02-14
通信作者: 曹贤武(1970-)，男，博士，教授，主要从事高分子材料加工与改性研究。 E-mail:ppeme@scut.edu.cn
作者简介:曹贤武(1970-)，男，博士，教授，主要从事高分子材料加工与改性研究。
基金资助:
国家重点研发计划项目 (2016YFB0302000)

Synthesis and Characterization of Quaternary Copolymerized Thermoplastic Polyimide

CAO Xianwu WEI Chuang HE Guangjian WEN Jiangwei

Guangdong Provincial Key Laboratory of Technique and Equipment for Macromolecular Advanced Manufacturing∥National Engineering
Research Center of Novel Equipment for Polymer Processing∥The Key Laboratory of Polymer Processing Engineering of Ministry of Education，South China University of Technology，Guangzhou 510640，Guangdong，China

Received:2019-10-17 Revised:2019-12-19 Online:2020-04-25 Published:2020-02-14
Contact: 曹贤武(1970-)，男，博士，教授，主要从事高分子材料加工与改性研究。 E-mail:ppeme@scut.edu.cn
About author:曹贤武(1970-)，男，博士，教授，主要从事高分子材料加工与改性研究。
Supported by:
Supported by the National Key Ｒesearch and Development Plan (2016YFB0302000)

摘要/Abstract

摘要： 为了提高聚酰亚胺的热塑性，制备兼具优异热塑性与耐热性的聚酰亚胺材料，以均苯四甲酸二酐 (PMDA) 与 3, 3', 4, 4'-联苯四羧酸二酐 (s-BPDA) 为二酐、4,4'-二氨基二苯醚 (ODA) 与 2,2'-二［4-(4-氨基苯氧基)苯基］丙烷 (BAPP) 为二胺，通过两步法成功制备了一系列四元共聚热塑性聚酰亚胺，并研究了刚性联苯基团与柔性单体、侧甲基的协同作用对聚酰亚胺材料性能的影响。利用 FTIＲ、XRD、DMA 和 TGA 等测试手段对材料的分子结构、热塑性和耐热性等进行了表征。结果表明: 该系列四元共聚聚酰亚胺具有良好的热塑性与耐热性，其中当二酐与二胺的摩尔分数比 (PMDA ∶s-BPDA∶ ODA ∶ BAPP) 为 70 ∶ 30 ∶ 70 ∶ 30 时，该材料表现出优异的热塑性和耐热性，同时在非质子极性溶剂中表现出较好的溶解性，极大地提高了聚酰亚胺在溶剂或熔融状态下的加工性能。

关键词: 热塑性聚酰亚胺, 四元共聚, BAPP, 热稳定性

Abstract: In order to improve the thermoplasticity of polyimide，a series of novel quaternary copolymerized poly-imide materials were successfully synthesized by two-step method with 1，2，4，5-benzenetetracarboxylic anhydride(PMDA) and 3，3'，4，4'-biphenyltetracarboxylic dianhydride ( s-BPDA) as dianhydride，4，4'-oxydianiline(ODA) and 2，2-bis［4-(4-aminophenoxy)phenyl］propane (BAPP) as diamine． The synergistic effect of rigid bi-phenyl groups with flexible monomers and pendant methyl groups on the properties of polyimide was studied． The molecular structure，thermoplasticity and heat resistance of the polyimides were characterized by FTIＲ，XRD，DMA，TGA and other testing methods． The results show that the series of quaternary copolymerized polyimides have good thermoplasticity and heat resistance． Particularly，when the molar fraction ratio of PMDA ∶ s-BPDA ∶ ODA ∶BAPP is 70 ∶ 30 ∶ 70 ∶ 30，the polyimide exhibits excellent thermoplasticity and heat resistance． What’s more，its good solubility in aprotic polar solvent can greatly improve the processing properties of the polyimide in a solvent or molten state．

Key words: thermoplastic polyimide, quaternary copolymerization, BAPP, heat resistance

曹贤武, 韦创, 何光建, 等. 四元共聚热塑性聚酰亚胺的合成与表征[J]. 华南理工大学学报（自然科学版）, 2020, 48(4): 73-79.

CAO Xianwu, WEI Chuang, HE Guangjian, et al. Synthesis and Characterization of Quaternary Copolymerized Thermoplastic Polyimide [J]. Journal of South China University of Technology (Natural Science Edition), 2020, 48(4): 73-79.

130

HTML			PDF

最新录用	在线预览	正式出版	最新录用	在线预览	正式出版
0	0	0	0	0	130

来源	本网站	其他网站

次数	115	15
比例	88%	12%

摘要

512

最新录用	在线预览	正式出版

8	2	502

来源	本网站	其他网站

次数	326	186
比例	64%	36%

[1]	廖俊旭鲁浩戴康徐曹华赵鸿斌韩利芬徐勇军方玉堂. 含氮润滑油添加剂的摩擦学性能[J]. 华南理工大学学报（自然科学版）, 2018, 46(7): 70-78.
[2]	肖新颜张登科. 异佛尔酮二异氰酸酯改性蒙脱土改性沥青的性能[J]. 华南理工大学学报（自然科学版）, 2017, 45(2): 116-121.
[3]	肖新颜张登科晏英朱文强. 有机蒙脱土/环氧树脂改性沥青材料的性能[J]. 华南理工大学学报（自然科学版）, 2015, 43(2): 139-143,150.
[4]	刘述梅冯猛孙志松赵建青袁彦超. 螺环-双环笼状磷酸酯的合成与性质[J]. 华南理工大学学报（自然科学版）, 2014, 42(10): 25-30.
[5]	叶君李文浩熊犍. 低pH 值下DACMC 的制备、结构及热性能[J]. 华南理工大学学报（自然科学版）, 2013, 41(6): 127-132.
[6]	肖新颜蔡锡松万彩霞. 交联型 FSiPUA 乳液的制备及涂膜性能[J]. 华南理工大学学报（自然科学版）, 2013, 41(10): 13-19.
[7]	李辉付时雨彭林才詹怀宇. 漆酶的层层自组装固定化及其酶学性质[J]. 华南理工大学学报（自然科学版）, 2011, 39(9): 158-164.
[8]	王小英刘博孙润仓吴军. 壳聚糖/累托石纳米复合材料的结构与性能[J]. 华南理工大学学报（自然科学版）, 2010, 38(9): 96-101.
[9]	方玉堂易立群刘艳山. 新型钛掺杂硅胶吸附材料的制备及性能[J]. 华南理工大学学报（自然科学版）, 2005, 33(10): 9-13.
[10]	陈炳炎, 陈东丹, 刘粤惠, 等. 混合碱效应对碲酸盐玻璃热稳定性的影响[J]. 华南理工大学学报(自然科学版), 2004, 32(4): 48-51.

四元共聚热塑性聚酰亚胺的合成与表征

Synthesis and Characterization of Quaternary Copolymerized Thermoplastic Polyimide

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 10

编辑推荐 0

Metrics

本文评价