液晶玻璃双刀轮切割及其裂纹产生、扩展规律

doi:10.3969/j.issn.1000-565X.2017.12.015

华南理工大学学报（自然科学版） ›› 2017, Vol. 45 ›› Issue (12): 99-105.doi: 10.3969/j.issn.1000-565X.2017.12.015

液晶玻璃双刀轮切割及其裂纹产生、扩展规律

万珍平¹ 张昆¹ 冯俊元¹ 卿剑波¹付永清²

1．华南理工大学机械与汽车工程学院，广东广州 510640; 2．华南理工大学设计学院，广东广州 510640

收稿日期:2017-03-22 修回日期:2017-06-15 出版日期:2017-12-25 发布日期:2017-10-31
通信作者: 万珍平(1971-)，男，博士，教授，主要从事切削、磨削加工工艺与装备等的研究． E-mail:zhpwan@scut.edu.cn
作者简介:万珍平(1971-)，男，博士，教授，主要从事切削、磨削加工工艺与装备等的研究．
基金资助:
国家自然科学基金资助项目(51775198)

Liquid Crystal Glass Substrate Cutting Based on Double Scribe-Wheels and Its Crack Initiation and Propagation Laws

WAN Zhen-ping¹ ZHANG Kun¹ FENG Jun-yuan¹ QING Jian-bo¹ FU Yong-qing²

1.School of Mechanical and Automotive Engineering,South China University of Technology,Guangzhou 510640,Guangdong,China; 2.School of Design,South China University of Technology,Guangzhou 510640,Guangdong,China

Received:2017-03-22 Revised:2017-06-15 Online:2017-12-25 Published:2017-10-31
Contact: 万珍平(1971-)，男，博士，教授，主要从事切削、磨削加工工艺与装备等的研究． E-mail:zhpwan@scut.edu.cn
About author:万珍平(1971-)，男，博士，教授，主要从事切削、磨削加工工艺与装备等的研究．
Supported by:
Supported by the National Natural Science Foundation of China(51775198)

摘要/Abstract

摘要： 液晶玻璃基板切割是液晶显示器制造的关键工艺之一．为了实现液晶玻璃基板的高效、高质量精密切割，提出了基于双刀轮的液晶玻璃基板切割新方法，即利用第一刀轮在待切割表面刻划出微塑性刻痕，再利用第二刀轮沿塑性刻痕切割玻璃．通过印压实验获得对称楔形压头印压液晶玻璃时仅产生塑性刻痕而不产生裂纹的临界载荷，然后研究对称楔形压头沿着第一次印压产生的塑性刻痕进行二次印压时裂纹的产生和扩展规律．结果表明: 二次印压没有横向裂纹产生，产生的垂直裂纹长度随一次印压载荷的增大略有增大，随二次印压载荷的增加线性增加; 无横向裂纹产生使得双刀轮切割时能够获得无边崩和微裂纹的、边缘整齐的断口形貌，垂直裂纹长度的增加使得双刀轮切割时无需二次裂片．

关键词: 液晶玻璃, 切割, 印压, 裂纹

Abstract: The liquid crystal display (LCD) glass substrate cutting is one of the key processes in manufacturing LCD screens.In order to achieve highly-efficient and high-quality precision cutting of LCD glass substrates,a new LCD glass substrate cutting method based on double scribe-wheels is proposed,in which the first scribe-wheel is used to scribe a plastic groove on the cutting surface and then the scribed LCD glass substrate is cut by the second scribe-wheel along the plastic groove.Then,the critical load of medial crack initiation is determined by the inden- tation experiments using a symmetric wedge,and the crack initiation and propagation laws during the second inden- tation of the symmetrical wedges along the plastic groove that is generated in the first indentation are investigated.Experimental results show that (1) no lateral cracks occur during the second indentation; (2) the length of the vertical cracks increases slightly with the increase of the load imposed in the first indentation,and it increases line- arly with the increase of the load imposed in the second indentation; (3) when no lateral cracks occur,it is possi- ble to obtain the perfect fractographs without edge chippings or microcracks ［1］; and (4) the length increase of the vertical cracks makes the splitting of the substrate on the flip side unnecessary during the second cutting based on the double scribe-wheels.

Key words: liquid crystal display glass, cutting, indentation, cracks

中图分类号:

TQ171

万珍平张昆冯俊元卿剑波付永清. 液晶玻璃双刀轮切割及其裂纹产生、扩展规律[J]. 华南理工大学学报（自然科学版）, 2017, 45(12): 99-105.

WAN Zhen-ping ZHANG Kun FENG Jun-yuan QING Jian-bo FU Yong-qing. Liquid Crystal Glass Substrate Cutting Based on Double Scribe-Wheels and Its Crack Initiation and Propagation Laws[J]. Journal of South China University of Technology (Natural Science Edition), 2017, 45(12): 99-105.

[1]	张占辉薛家祥. 熔滴冲击方向对焊缝质量的影响[J]. 华南理工大学学报（自然科学版）, 2019, 47(4): 138-144.
[2]	吕东喜张远明沈圣成. 玻璃孔加工入口破损形成机理[J]. 华南理工大学学报（自然科学版）, 2018, 46(7): 79-84.
[3]	杨大勇万珍平陆龙生. 粉末冶金生坯边位印压的裂纹扩展行为 [J]. 华南理工大学学报（自然科学版）, 2018, 46(3): 23-28.
[4]	伍希志程军圣杨宇黄毅. CFRP 加固裂纹钢板的疲劳寿命及加固参数研究[J]. 华南理工大学学报（自然科学版）, 2016, 44(4): 143-148.
[5]	薛小锋郑香伟冯蕴雯冯元生 . 基于变载荷间隔的 MSD 结构疲劳可靠性研究[J]. 华南理工大学学报（自然科学版）, 2015, 43(11): 145-150.
[6]	张仕伟万珍平欧元贤徐培杰汤勇. 石墨边位印压裂纹的产生和扩展规律[J]. 华南理工大学学报（自然科学版）, 2014, 42(9): 12-17.
[7]	陆念力詹伟刚. 基于等效初始缺陷尺寸和功率谱法的起重机疲劳寿命预测[J]. 华南理工大学学报（自然科学版）, 2014, 42(4): 118-123,130.
[8]	韩强王彩红辛东嵘. 含中心裂纹石墨烯拉伸性能的分子动力学模拟[J]. 华南理工大学学报（自然科学版）, 2014, 42(4): 52-58.
[9]	韩强王彩红姚小虎. 含裂纹碳纳米管轴压性能的分子动力学模拟[J]. 华南理工大学学报（自然科学版）, 2014, 42(12): 133-140.
[10]	赵传宇黄培彦罗毅. 受拉 FRP 加固 X80 钢板中表面裂纹应力强度因子的数值分析[J]. 华南理工大学学报（自然科学版）, 2013, 41(8): 109-114.
[11]	段先云阮锋张赛军. 水平与垂直晶界铜双晶的压缩形貌观察与分析[J]. 华南理工大学学报（自然科学版）, 2013, 41(7): 7-12.
[12]	王硕苏玉民杜欣. 滑行艇静水直航及波浪中运动的数值模拟[J]. 华南理工大学学报（自然科学版）, 2013, 41(4): 119-126.
[13]	张术宽黄培彦赵传宇. CFL 加固受弯钢板中表面裂纹应力强度因子的数值分析[J]. 华南理工大学学报(自然科学版), 2012, 40(4): 162-168.
[14]	吴运新龚海廖凯. 铝合金预拉伸板残余应力场的评估模型[J]. 华南理工大学学报（自然科学版）, 2011, 39(1): 90-94.
[15]	张衡魏德敏. 分形裂纹的断裂参数[J]. 华南理工大学学报（自然科学版）, 2010, 38(3): 12-16.

液晶玻璃双刀轮切割及其裂纹产生、扩展规律

Liquid Crystal Glass Substrate Cutting Based on Double Scribe-Wheels and Its Crack Initiation and Propagation Laws

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价