电脉冲处理对硅黄铜耐蚀性能的影响

doi:10.3969/j.issn.1000-565X.2015.07.005

华南理工大学学报（自然科学版） ›› 2015, Vol. 43 ›› Issue (7): 28-32,67.doi: 10.3969/j.issn.1000-565X.2015.07.005

电脉冲处理对硅黄铜耐蚀性能的影响

赵作福¹齐锦刚²王建中²刘兴江² 王家毅²

1. 北京科技大学冶金与生态工程学院，北京 100083; 2. 辽宁工业大学材料科学与工程学院，辽宁锦州 121001

收稿日期:2014-10-28 修回日期:2015-04-16 出版日期:2015-07-25 发布日期:2015-06-03
通信作者: 赵作福( 1978-) ，男，博士，主要从事外场作用下金属凝固理论及应用研究. E-mail:zzf197810089927@163.com
作者简介:赵作福( 1978-) ，男，博士，主要从事外场作用下金属凝固理论及应用研究.
基金资助:
国家自然科学基金资助项目( 51354001) ; 辽宁省教育厅项目( LZ2014031) ; 辽宁省教育厅团队项目( LT2013014)

Effects of Electric Pulse Treatment on Corrosion Resistance of Silicon Brass

Zhao Zuo-fu¹Qi Jin-gang²Wang Jian-zhong² Liu Xing-jiang² Wang Jia-yi²

1. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China; 2. School of Materials Science and Engineering, Liaoning University of Technology, Jinzhou 121001, Liaoning, China

Received:2014-10-28 Revised:2015-04-16 Online:2015-07-25 Published:2015-06-03
Contact: 赵作福( 1978-) ，男，博士，主要从事外场作用下金属凝固理论及应用研究. E-mail:zzf197810089927@163.com
About author:赵作福( 1978-) ，男，博士，主要从事外场作用下金属凝固理论及应用研究.
Supported by:
Supported by the National Natural Science Foundation of China( 51354001)

摘要/Abstract

摘要： 采用电化学工作站和扫描电子显微镜等研究了电脉冲处理对硅黄铜合金耐蚀性能的影响．研究结果表明: 经电脉冲处理后，硅黄铜合金的腐蚀电位略有提高，自腐蚀电流密度下降约一个数量级; 容抗弧直径大小是未处理时的6 ～ 7 倍，其脱锌层厚度由未处理时的80 ～ 90μm 减小到电脉冲处理后的15 ～ 20μm．电脉冲处理后硅黄铜合金的耐蚀性优于未进行电脉冲处理的硅黄铜合金．

关键词: 电脉冲处理, 硅黄铜, 耐蚀性能, 腐蚀电位, 自腐蚀电流密度

Abstract: The effects of the electric pulse treatment on the corrosion resistance of silicon brass are investigated by using an electrochemical workstation and a SEM. The results show that, after the electric pulse treatment, the corrosion potential of silicon brass increases while the corrosion current density decreases by about one order of magnitude, and that the electric field treatment increases the capacitive reactance diameter of silicon brass by 5~6 times and decreases the thickness of dezincification layer from 80~90 μm to 15~20 μm. It is thus concluded that the corrosion resistance of silicon brass alloy is improved after the electric field treatment.

Key words: electric pulse treatment, silicon brass, corrosion resistance, corrosion potential, corrosion current density

中图分类号:

中图分类号：TG174.3+6

赵作福齐锦刚王建中刘兴江王家毅. 电脉冲处理对硅黄铜耐蚀性能的影响[J]. 华南理工大学学报（自然科学版）, 2015, 43(7): 28-32,67.

Zhao Zuo-fu Qi Jin-gang Wang Jian-zhong Liu Xing-jiang Wang Jia-yi. Effects of Electric Pulse Treatment on Corrosion Resistance of Silicon Brass[J]. Journal of South China University of Technology (Natural Science Edition), 2015, 43(7): 28-32,67.

[1]	左茜李文芳穆松林. 常温下添加剂对有色Ti-Zr转化膜形貌与性能的影响[J]. 华南理工大学学报（自然科学版）, 2014, 42(10): 7-13.
[2]	张军军李文芳杜军. 常温时添加剂对Ce-Mn转化膜的影响[J]. 华南理工大学学报（自然科学版）, 2010, 38(4): 76-82.
[3]	许乔瑜桂艳卢锦堂孔纲车淳山 . 热浸Zn—Ti合金镀层的显微组织与耐蚀性能[J]. 华南理工大学学报（自然科学版）, 2008, 36(7): 82-86.

电脉冲处理对硅黄铜耐蚀性能的影响

Effects of Electric Pulse Treatment on Corrosion Resistance of Silicon Brass

PDF

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 3

编辑推荐

Metrics

本文评价