NucIeation Mechanism and ParticIe Size Distribution in Semi-Continuous Emulsion Polymerization with Different Monomer Ratios

Zhang Xin-ya Jiang Qing-mei Sun Zhi-juan Lan Ren-hua Chen Huan-qin

Research InstÏtute of Chemical Engineering , South China Univ. of Tech. , Guangzhou 510640 , Guangdong , China

Received:2006-06-27 Online:2007-06-25 Published:2007-06-25
Contact: 张心亚(1974-)，男，副教授，主要从事水性涂料及乳液合成研究. E-mail:cexyzh@scut. edu.cn
About author:张心亚(1974-)，男，副教授，主要从事水性涂料及乳液合成研究.
Supported by:
广东省科技计划项目( 2003B10506 )

摘要/Abstract

摘要： 以甲基丙烯酸甲酯(MMA) 和丙烯酸丁酯(BA) 为反应单体、过硫酸苦甲(KPS) 为引发剂、十二烷基苯磺酸纳(DBS) 为乳化剂，研究了半连续乳液聚合中单体配比F(MMAl BA 的质量比)对体系成核机理和粒径分布的影响.结果表明:在F 较大(≥0.75 )时，体系以均相成核与胶束成核两种方式成核， F 较小(≤0.5) 时，体系主要以胶束成核方式成核jBA 、MMA 单体均聚合成的乳液粒径小于其共聚时的粒径;成核阶段结束时的转化率突变、颜色突变、粒径突变规律是一一对应的.

关键词: 半连续乳液聚合, 成核机理, 粒径分布, 单体配比

Abstract:

The effect of the mass ratio of methyl methacrylate (MMA) to butyl acrylate (BA) , namely F , on the nucleation mechanism and the particle size distribution in semi-continuous emulsion polymerization was investigated, with MMA and BA as the monomers , potassium persulfate (KPS) as the initiator and sodium dodecyl benzene sulfonate (DBS) as the emulsifier. The results show that (1) the nucleation mechanism of the system is both homogeneous nucleation and micelle nucleation when F is more than 0. 75 , while remaining mainly micelle nucleation when F is less than 0. 5; (2) the particle size of the resulted latex in the homo-polymerization system is smaller than that in the co-polymerization system; and (3) the abrupt transition disciplinarians of the conversion rate , the color and the particle size are correlative to each other at the end of the nucleation process.

Key words: semi-continuous emulsion polymerization, nucleation mechanism, particle size distribution, monomerratio

张心亚江庆梅孙志娟蓝仁华陈焕钦. 不同单体配比下半连续乳液聚合的成核机理和粒径分布[J]. 华南理工大学学报（自然科学版）, 2007, 35(6): 71-75.

Zhang Xin-ya Jiang Qing-mei Sun Zhi-juan Lan Ren-hua Chen Huan-qin. NucIeation Mechanism and ParticIe Size Distribution in Semi-Continuous Emulsion Polymerization with Different Monomer Ratios[J]. Journal of South China University of Technology (Natural Science Edition), 2007, 35(6): 71-75.

[1]	侯献军许京刘近平杜松泽李孟孟. 柴油机燃用柴油/乙醇混合燃料的颗粒排放特性[J]. 华南理工大学学报（自然科学版）, 2016, 44(9): 144-150.
[2]	宋丹青项国圣. 城市垃圾炉渣变形特性的三轴试验[J]. 华南理工大学学报（自然科学版）, 2016, 44(7): 116-122.
[3]	叶君李文浩熊犍. 不同 pH 值下制备的 CMC/Eu 纳米络合粒子的粒径及其分布与粒子荧光性质的关系[J]. 华南理工大学学报（自然科学版）, 2014, 42(6): 73-78,120.
[4]	胡小芳胡大为吴成宝. 多孔介质粘土颗粒群的粒径分布分形维[J]. 华南理工大学学报（自然科学版）, 2006, 34(5): 99-102.
[5]	张静涂伟萍胡剑青. 核壳型丙烯酸酯类反应性微凝胶胶粒的粒径及分布[J]. 华南理工大学学报（自然科学版）, 2006, 34(3): 72-76.