Fire Resistance of Bolted Steel-Glulam-Steel Connections

Zhang Jin¹ Xu Qing-feng² Bai Yi-wei¹ Cai Jian-guo¹

1． Key Laboratory of Concrete ＆ Prestressed Concrete Structures of the Ministry of Education，Southeast University，Nanjing 210096，Jiangsu，China; 2． Shanghai Key Laboratory of Engineering Structure Safety，Shanghai Ｒesearch Institute of Building Sciences，Shanghai 200032，China

Received:2014-06-06 Revised:2014-09-10 Online:2015-02-25 Published:2014-12-31
Contact: 张晋(1974-)，男，博士，副教授，主要从事木结构体系、预应力结构体系研究． E-mail:zhangjin0622@139.com
About author:张晋(1974-)，男，博士，副教授，主要从事木结构体系、预应力结构体系研究．
Supported by:
Supported by the National Natural Science Foundation of China(51178115)and the Natural Science Foundtion of Jiangsu Province(BK2012239)

摘要/Abstract

摘要： 为研究我国常用树种胶合木钢夹板螺栓连接节点的抗火性能，进行了 4 个胶合木钢夹板螺栓连接试件的炭化速度试验，以及两组(共 8 个)胶合木钢夹板螺栓连接试件在不同持荷水平下的耐火极限试验．结果表明:钢夹板边缘内侧区域木材的炭化速度小于钢夹板边缘外侧区域，不同截面的水平向炭化速度小于竖向炭化速度，炭化速度随着受火时间的延长有降低的趋势;试件端距达到规范要求后，将端距从 7d 增加到 10d 并不能明显提高耐火极限，耐火极限随着持荷水平的增加而明显降低;其他条件相同时，耐火极限试件升温快于炭化速度试件．

关键词: 胶合木钢夹板螺栓连接, 炭化速度, 耐火极限, 抗火性能

Abstract: In order to reveal the fire resistance of bolted steel-glulam-steel connections using common tree species in China as the material，four connection specimens were tested to obtain the corresponding charring rates，and two groups of (eight) specimens were tested to reveal their fire endurance in different load levels． It is found that (1) the charring rate of interior area at steel splint edge is lower than that of external area; (2) the horizontal charring rate is lower than the vertical one in different cross sections; (3) the charring rate tends to reduce with the prolon-ging of fire duration; (4) changing the end-to-end distance from 7d to 10d cannot remarkably improve the fire en-durance limit of the bolted connections when the distance meets the regulatory requirements; (5) the fire endurance limit of the connections significantly decreases with the increase of load level; and (6) in the same conditions，the temperature rise of specimens in fire endurance tests is higher than that in charring rate tests．

Key words: bolted steel-glulam-steel connection, charring rate, fire endurance limit, fire resistance

中图分类号:

TU366.2 TU352.5

张晋许清风柏益伟蔡建国. 胶合木钢夹板螺栓连接节点的抗火性能[J]. 华南理工大学学报（自然科学版）, 2015, 43(2): 58-65.

Zhang Jin Xu Qing-feng Bai Yi-wei Cai Jian-guo. Fire Resistance of Bolted Steel-Glulam-Steel Connections[J]. Journal of South China University of Technology (Natural Science Edition), 2015, 43(2): 58-65.

[1]	张晋, 刘得龙, 张强, 等. 正交胶合木墙体耐火极限试验及数值模拟[J]. 华南理工大学学报（自然科学版）, 2021, 49(4): 9-19.
[2]	吴波梁悦欢. 高温下钢筋和混凝土强度随机性对柱耐火极限的影响[J]. 华南理工大学学报（自然科学版）, 2009, 37(9): 1-6.
[3]	吴波万志军. 碳纤维布抗弯加固钢筋混凝土梁的耐火性能试验[J]. 华南理工大学学报（自然科学版）, 2009, 37(8): 76-82，88.
[4]	徐玉野吴波. 钢筋混凝土L 形柱的耐火极限[J]. 华南理工大学学报（自然科学版）, 2007, 35(7): 110-115,130.
[5]	吴波洪洲. 钢筋混凝土简支梁的耐火极限[J]. 华南理工大学学报（自然科学版）, 2006, 34(7): 82-87.
[6]	吴波洪洲. 高强混凝土柱的耐火极限[J]. 华南理工大学学报（自然科学版）, 2006, 34(11): 64-69.

胶合木钢夹板螺栓连接节点的抗火性能

Fire Resistance of Bolted Steel-Glulam-Steel Connections

PDF

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 6

编辑推荐

Metrics

本文评价