壳聚糖／纳米SiOx复合膜的制备及机械性能

华南理工大学学报（自然科学版） ›› 2008, Vol. 36 ›› Issue (7): 36-41.

壳聚糖／纳米SiOx复合膜的制备及机械性能

王明力¹司方¹张义明¹赵德刚²

1. 贵州大学贵州省发酵工程与生物制药重点实验室, 贵州贵阳 550003；2. 贵州大学绿色农药与农业生物工程教育部重点实验室, 贵州贵阳 550025

收稿日期:2007-12-19 修回日期:2008-03-17 出版日期:2008-07-25 发布日期:2008-07-25
通信作者: 王明力（1961-），女，教授，主要从事生物材料的研究． E-mail:wmlgycn@tom．com
作者简介:王明力（1961-），女，教授，主要从事生物材料的研究．
基金资助:
贵州省优秀科技教育人才省长基金资助项目（200619）;贵州省科技攻关项目（NGY065）

Preparation and Mechanical Properties of Composite Chitosan/Nano-Sized SiOx Film

Wang Ming-li¹ Si Fang¹ Zhang Yi-ming¹ Zhao De-gang²

1. Gnizhou Province Key Laboratory of Fermentation Engineering and Bio-Pharmacy, Gnizhou University, Guizhou 550003, Guiyang, China; 2. Key Laboratory of Green Pesticide and Agricultural Biological Engineering of the Ministry of Education, Guizhou University, Guizhou 550025, Guiyang, China

Received:2007-12-19 Revised:2008-03-17 Online:2008-07-25 Published:2008-07-25
Contact: 王明力（1961-），女，教授，主要从事生物材料的研究． E-mail:wmlgycn@tom．com
About author:王明力（1961-），女，教授，主要从事生物材料的研究．
Supported by:
贵州省优秀科技教育人才省长基金资助项目（200619）;贵州省科技攻关项目（NGY065）

摘要/Abstract

摘要： 采用二次回归旋转正交试验方法，探讨了制备壳聚糖／纳米SiOx复合膜的优化工艺条件，用流延法制得分散比较均匀的纳米复合膜，并对涂膜结构进行红外光谱（IR）、X射线衍射（XRD）及透射电镜（TEM）表征．结果表明：复合膜（CTS—SiOx）中壳聚糖与SiO，粒子表面的大量羟基存在强烈的氢键作用；当配料为壳聚糖1．98g、SiOx0．017g、单甘酯0．04g时，壳聚糖复合涂膜拉伸强度达到最优值、与纯壳聚糖单膜相比，复合膜的拉伸强度、断裂伸长率和直角撕裂强度分别提高了63．3％，45．4％和11．6％，透水率降低了73．1％．可见复合膜的性能优于单膜．

关键词: 壳聚糖, 复合膜, 拉伸强度, 二次回归旋转正交试验

Abstract:

The preparation conditions of composite chitosan/nano-sized SiOx （ CTS-SiOx） films were optimized by quadratic-regression rotatable orthogonal experiments, and the films with homogeneous structure were prepared via the casting method, which were then characterized by means of IR, XRD and TEM. The results show that there are a great number of hydrogen bonds between chitosan and the hydroxyls on nano-sized SiOx surface, that the CTS- SiOx film with a chitosan/SiO/glycerel monostearte mass ratio of 1.98： 0. 017：0.04 has a maximum tensile strength, and that, as compared with the chitosan film, the tensile strength, breaking extensibility and orthogonaltear strength of the composite film increase respectively by 63.3% , 45.4% and 11.6% , while the water permeability decreases by 73.1%. It is thus concluded that the composite film is superior to the film with single component.

Key words: chitosan, composite film, tensile strength, quadratic-regression rotatable orthogonal experiment

王明力司方张义明赵德刚 . 壳聚糖／纳米SiOx复合膜的制备及机械性能[J]. 华南理工大学学报（自然科学版）, 2008, 36(7): 36-41.

Wang Ming-li Si Fang Zhang Yi-ming Zhao De-gang . Preparation and Mechanical Properties of Composite Chitosan/Nano-Sized SiOx Film[J]. Journal of South China University of Technology (Natural Science Edition), 2008, 36(7): 36-41.

[1]	赵振刚刘爽游丽君. 壳聚糖修饰甜菜红素脂质体的制备与抗肿瘤活性[J]. 华南理工大学学报（自然科学版）, 2022, 50(1): 16-22.
[2]	赵振刚韩德侠. 活性炭负载壳聚糖对水中腐殖酸的吸附性能及吸附机理[J]. 华南理工大学学报(自然科学版), 2018, 46(10): 141-148.
[3]	肖敏敏. 沥青填入式伸缩缝混合料组成设计及界面性能[J]. 华南理工大学学报（自然科学版）, 2016, 44(8): 106-113.
[4]	彭新文谭杰文吴昌艳邓青林佳纯孙润仓. 半纤维素-g-壳聚糖负载钯(0)催化剂的制备与催化性能[J]. 华南理工大学学报（自然科学版）, 2016, 44(6): 27-34,40.
[5]	郑大锋李小康于凡哲陈然. 玉米秸秆酶解木质素的化学结构及在环氧树脂中的应用[J]. 华南理工大学学报（自然科学版）, 2016, 44(11): 26-32.
[6]	殷小春汤邦曾文兵杨智韬瞿金平. 不同流场特性下的PS/HDPE共混物性能[J]. 华南理工大学学报（自然科学版）, 2014, 42(10): 36-43.
[7]	袁毅桦雷莉何慧贾德民. 环氧氯丙烷交联壳聚糖/海藻酸钠吸附铜离子的研究[J]. 华南理工大学学报(自然科学版), 2012, 40(7): 148-154.
[8]	周建芹陈韶华. 智能凝胶载体固定化纤维素酶提取植物活性成分[J]. 华南理工大学学报(自然科学版), 2012, 40(1): 125-130,137.
[9]	刘凯何北海黎小敏赵光磊. 交联壳聚糖的制备及对聚半乳糖醛酸的吸附[J]. 华南理工大学学报（自然科学版）, 2011, 39(1): 74-78.
[10]	王小英刘博孙润仓吴军. 壳聚糖/累托石纳米复合材料的结构与性能[J]. 华南理工大学学报（自然科学版）, 2010, 38(9): 96-101.
[11]	王小英刘博林鹿吴军孙润仓. 新型纳米复合材料作为非病毒基因载体的研究[J]. 华南理工大学学报（自然科学版）, 2010, 38(5): 133-138.
[12]	葛华才黄仕英梁恺. 壳聚糖改性微球的微波辐射制备及吸附性能[J]. 华南理工大学学报（自然科学版）, 2009, 37(6): 27-30，36.
[13]	段丽红杨晋青叶盛权陈松伟郭祀远 . 磁场作用下壳聚糖希夫碱对铬离子的吸附性能[J]. 华南理工大学学报（自然科学版）, 2009, 37(4): 130-133.
[14]	卢锦堂张双红孔纲车淳山. 镀锌钢上钼酸盐／硅烷复合膜的组成与耐蚀性[J]. 华南理工大学学报（自然科学版）, 2009, 37(12): 12-17.
[15]	蒋寅王兆梅叶盛权郭桦郭祀远. 外加物理场对壳聚糖-亚铁配合反应的影响[J]. 华南理工大学学报（自然科学版）, 2008, 36(7): 62-66,71.