剑麻纤维增强PBS复合材料的流变性能

doi:10.3969/j.issn.1000-565X.2010.07.018

华南理工大学学报（自然科学版） ›› 2010, Vol. 38 ›› Issue (7): 101-106.doi: 10.3969/j.issn.1000-565X.2010.07.018

剑麻纤维增强PBS复合材料的流变性能

冯彦洪^1,2 李展洪^1,2 瞿金平^1,2 刘斌^1,2 徐百平³ 王宗明^1,2

1.华南理工大学聚合物新型成型装备国家工程研究中心, 广东广州 510640； 2.华南理工大学聚合物成型加工工程教育部重点实验室, 广东广州 510640； 3.广东轻工职业技术学院轻化工程系, 广东广州 510300

收稿日期:2009-09-09 修回日期:2010-03-23 出版日期:2010-07-25 发布日期:2010-07-25
通信作者: 冯彦洪（1976-）,女,副教授,博士,主要从事新型聚合物制备成型方法及设备研究. E-mail: yhfeng@scut.edu.cn
作者简介:冯彦洪（1976-）,女,副教授,博士,主要从事新型聚合物制备成型方法及设备研究.
基金资助:
国家自然科学基金资助项目（50903033 10872071）; 国家科技支撑计划项目（2009BAI84B05 2009BAI84B06）; 广州市科技计划项目（2007Z2-D9151）; 华南理工大学中央高校基本科研业务费资助项目（2009ZM0317）

Rheological Properties of PBS Composites Reinforced with Sisal Fibers

Feng Yan-hong ^1.2 Li Zhan-hong ^1.2 Qu Jin-ping ^1.2 Liu Bin ^1.2 Xu Bai-ping³ Wang Zong-ming ^1.2

1. National Engineering Research Center of Novel Equipment for Polymer Processing,South China University of Technology, Guangzhou 510640,Guangdong,China; 2. Key Laboratory of Polymer Processing Engineering of the Ministry of Education, South China University of Technology,Guangzhou 510640,Guangdong,China; 3. Department of Chemical Engineering, Guangdong Industry Technical College,Guangzhou 510300,Guangdong,China

Received:2009-09-09 Revised:2010-03-23 Online:2010-07-25 Published:2010-07-25
Contact: 冯彦洪（1976-）,女,副教授,博士,主要从事新型聚合物制备成型方法及设备研究. E-mail: yhfeng@scut.edu.cn
About author:冯彦洪（1976-）,女,副教授,博士,主要从事新型聚合物制备成型方法及设备研究.
Supported by:
国家自然科学基金资助项目（50903033 10872071）; 国家科技支撑计划项目（2009BAI84B05 2009BAI84B06）; 广州市科技计划项目（2007Z2-D9151）; 华南理工大学中央高校基本科研业务费资助项目（2009ZM0317）

摘要/Abstract

摘要： 植物纤维与聚合物复合体系不适宜用毛细管流变仪测量流变性能.为此,文中建立一种利用转矩流变仪测量流变特性的方法,利用该方法表征了不同剑麻纤维质量分数下,聚丁二酸丁二醇酯（PBS）复合材料的流变性能,并测量实验后纤维的长径比,分析剑麻纤维质量分数和转速对复合材料中纤维长径比以及复合材料弯曲强度的影响.结果表明,由于纤维的解缠、断裂和取向,复合材料的剪切变稀现象随剑麻纤维质量分数的增加而更为明显.

关键词: 剑麻, 聚丁二酸丁二醇酯, 转矩流变仪, 流变性能

Abstract:

As the capillary rheometer is not appropriate for measuring the rheological properties of the composites of plant fibers and polymers,a new measurement method using the torque rheometer was proposed and was then used to measure the rheological properties of polybuthylene succinate （ PBS） composites reinforced with sisal fibers （ SF） in different mass fractions. Then,the length-to-diameter ratio of sisal fibers in the composites was measured,and the effects of SF content and rotor speed on the length-to-diameter ratio of SF and the flexural strength of the composites were analyzed. The results show that the shear-thinning phenomenon of the composites becomes more significant with the increase in SF content due to the disentangling,breaking and orientation of SF.

Key words: sisal, polybuthylene succinate, torque rheometer, rheological property

冯彦洪李展洪瞿金平刘斌徐百平王宗明 . 剑麻纤维增强PBS复合材料的流变性能[J]. 华南理工大学学报（自然科学版）, 2010, 38(7): 101-106.

Feng Yan-hong Li Zhan-hong Qu Jin-ping Liu Bin Xu Bai-ping Wang Zong-ming . Rheological Properties of PBS Composites Reinforced with Sisal Fibers[J]. Journal of South China University of Technology (Natural Science Edition), 2010, 38(7): 101-106.

[1]	赵永青陈福泉吴正环冯彦洪晋刚瞿金平. PBS /ESO 共混物的力学和流变学性能[J]. 华南理工大学学报（自然科学版）, 2013, 41(10): 103-107,116.
[2]	范方强夏正斌李清英李忠陈焕钦. 成膜物质对水性防火涂料膨胀阻燃性能的影响[J]. 华南理工大学学报(自然科学版), 2012, 40(9): 26-31,37.
[3]	卢珣林艳梅吴叔青田敏. 动态硫化TPEE /ACM/纳米SiO₂复合材料的制备[J]. 华南理工大学学报(自然科学版), 2012, 40(7): 135-141.
[4]	李方贤韦江雄王辉诚王景平裴新意余其俊. 胶凝材料用量对新拌自密实混凝土性能的影响[J]. 华南理工大学学报(自然科学版), 2012, 40(4): 79-84.
[5]	彭新文任俊莉孙润仓. 高取代度木聚糖衍生物的理化性质[J]. 华南理工大学学报（自然科学版）, 2011, 39(8): 82-86.
[6]	刘斌骆接文瞿金平蔡一湘. 振动力场对金属粉末注射熔体流变性能及相分离的影响[J]. 华南理工大学学报（自然科学版）, 2010, 38(6): 146-150.

剑麻纤维增强PBS复合材料的流变性能

Rheological Properties of PBS Composites Reinforced with Sisal Fibers

PDF

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 6

编辑推荐

Metrics

本文评价