电致变色聚噻吩及其固态电致变色器件的制备

doi:10.3969/j.issn.1000-565X.2010.07.017

华南理工大学学报（自然科学版） ›› 2010, Vol. 38 ›› Issue (7): 97-100.doi: 10.3969/j.issn.1000-565X.2010.07.017

电致变色聚噻吩及其固态电致变色器件的制备

刘平¹ 王娟¹ 关丽^1,2 腊明¹蒋传煜¹ 童真¹ 邓文基³

1.华南理工大学材料科学研究所, 广东广州 510640；2.广东药学院药科学院, 广东广州 510006；3.华南理工大学物理系, 广东广州 510640

收稿日期:2009-12-04 修回日期:2010-02-21 出版日期:2010-07-25 发布日期:2010-07-25
通信作者: 刘平（1962-）,男,教授,博士,主要从事有机/高分子材料研究 E-mail: mcpliu@scut.edu.cn
作者简介:刘平（1962-）,男,教授,博士,主要从事有机/高分子材料研究.
基金资助:
国家自然科学基金资助项目（20774031）; 广东省科技计划资助项目（2006A10702003 2009B090300025）

Preparation of Electrochromic Polythiophene and Fabrication of Corresponding Solid-State Electrochromic Device

Liu Ping¹ Wang Juan¹ Guan Li ^1.2 La Ming¹ Jiang Chuan-yu¹ Tong Zhen¹ Deng Wen-ji ³

1. Research Institute of Materials Science,South China University of Technology,Guangzhou 510640,Guangdong,China; 2. School of Pharmacy,Guangdong Pharmaceutical College,Guangzhou 510006,Guangdong,China; 3. Department of Physics,South China University of Technology,Guangzhou 510640,Guangdong,China

Received:2009-12-04 Revised:2010-02-21 Online:2010-07-25 Published:2010-07-25
Contact: 刘平（1962-）,男,教授,博士,主要从事有机/高分子材料研究 E-mail: mcpliu@scut.edu.cn
About author:刘平（1962-）,男,教授,博士,主要从事有机/高分子材料研究.
Supported by:
国家自然科学基金资助项目（20774031）; 广东省科技计划资助项目（2006A10702003 2009B090300025）

摘要/Abstract

摘要： 以2,2＇：5＇,2″-三噻吩（3T）作为单体,通过电化学聚合制备了聚噻吩,研究了聚噻吩薄膜的电致变色性能.研究发现,在液体电解质中,当施加外加电压时,聚噻吩薄膜的颜色能发生橙黄色和藏青色的可逆变化.利用聚噻吩作为电致变色活性层制备了固态电致变色器件ITO/聚噻吩/凝胶电解质/ITO,在施加外加电压时,固态电致变色器件也能发生橙黄色和藏青色的可逆变化.态电致变色器件

关键词: 电化学聚合, 聚噻吩, 电致变色, 固态电致变色器件

Abstract:

Polythiophene was prepared via the electropolymerization of 2,2＇∶ 5＇,2″-terthiophene （ 3T） ,and the electrochromic behaviors of polythiophene film were investigated,revealing a reversible color change from orange yellow to navy blue for the film with applied voltage in liquid electrolyte. Moreover,a solid-state electrochromic indium tin oxide （ ITO） /polythiophene/conducting gel/ITO device was fabricated,with polythiophene as the active electrochromic layer,and a similar color change was also observed for the device with applied voltage.

Key words: electropolymerization, polythiophene, electrochromic behavior, solid-state electrochromic device

王娟关丽蒋传煜腊明刘平童真邓文基. 电致变色聚噻吩及其固态电致变色器件的制备[J]. 华南理工大学学报（自然科学版）, 2010, 38(7): 97-100.

Liu Ping Wang Juan Guan Li La Ming Jiang Chuan-yu Tong Zhen Deng Wen-ji . Preparation of Electrochromic Polythiophene and Fabrication of Corresponding Solid-State Electrochromic Device[J]. Journal of South China University of Technology (Natural Science Edition), 2010, 38(7): 97-100.

[1]	陈明洁沈辉. 热处理下光电致变色器件的结构和变色性能[J]. 华南理工大学学报(自然科学版), 2004, 32(6): 31-35.
[2]	刘平胡建华赵其中周小平童真许运华邓文基 . 低聚噻吩衍生物的合成及液晶性能[J]. 华南理工大学学报(自然科学版), 2003, 31(5): 11-15.

电致变色聚噻吩及其固态电致变色器件的制备

Preparation of Electrochromic Polythiophene and Fabrication of Corresponding Solid-State Electrochromic Device

PDF

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 2

编辑推荐

Metrics

本文评价