Preparation and Properties of Polyvinyl Formal for Vacuum Sealing Drainage

Guo Sen Ma Tian- cong Zou Yong- kun Liu Fang He Jing- wei   

  1. School of Materials Science and Engineering,South China University of Technology,Guangzhou 510640,Guangdong,China
  • Received:2013-10-30 Revised:2013-12-09 Online:2014-06-25 Published:2014-05-01
  • Contact: 何经纬(1982-)，男，博士，讲师，主要从事生物医用高分子材料研究． E-mail:msjwhe@scut.edu.cn
  • About author:郭森(1989-)，男，博士生，主要从事生物医用高分子材料研究．E-mail:guo0395@126．com
  • Supported by:

    广东省自然科学基金重点项目(S2011020001452)

PDF

184

Abstract:

Polyvinyl formal,a kind of foam material for vacuum sealing drainage,was synthesized via a mechanicalmixing and foaming approach,with polyvinyl alcohol,methanal,starch,sodium dodecyl sulfate (SDS) and sulfu-ric acid as materials.Then,the effects of stirring speed,SDS content,curing temperature and starch dosage on thewater absorbency,tensile property,pore size and pore size distribution of the product were investigated.The resultsshow that (1) the water absorbency of the synthesized foam material increases with the SDS content ranging from 0.0 to 2.0 g; (2) the mechanical properties of the material become stable when SDS content is more than 1.0 gbut dramatically degrade with the increase of starch dosage and curing temperature; (3) higher stirring speed mayresult in smaller pore and more uniform pore size distribution; (4) more SDS may lead to more large pores and wi-der pore size distribution; and (5) the number of pores is not strictly related to starch dosage.

Key words: vacuum sealing drainage, polyvinyl formal, foam material, water absorbency, tensile property, pore size, pore size distribution