海藻酸钠的提纯及海藻酸钙多孔支架的制备

华南理工大学学报(自然科学版) ›› 2012, Vol. 40 ›› Issue (7): 142-147.

海藻酸钠的提纯及海藻酸钙多孔支架的制备

刘杨任力^† 季培红王迎军

华南理工大学材料科学与工程学院∥国家人体组织功能重建工程技术研究中心∥广东省生物医学工程重点实验室，广东广州 510640

收稿日期:2012-02-11 修回日期:2012-04-10 出版日期:2012-07-25 发布日期:2012-06-01
通信作者: 任力(1973-) ，男，教授，博士生导师，主要从事生物医用材料和组织工程研究． E-mail: psliren@scut．edu．cn E-mail:liuyang_cug@ yahoo.com.cn
作者简介:刘杨(1985-) ，男，博士生，主要从事高分子材料、生物医用材料研究．
基金资助:
国家自然科学基金重点项目( 50732003; 50803018)

Purification of Sodium Alginate and Preparation of Porous Calcium Alginate Scaffolds

Liu Yang Ren Li Ji Pei-hong Wang Ying-jun

School of Materials Science and Engineering∥National Engineering Research Center for Tissue Restoration and Reconstruction∥Guangdong Province Key Laboratory of Biomedical Sciences and Engineering,South China University of Technology,Guangzhou 510640,Guangdong,China

Received:2012-02-11 Revised:2012-04-10 Online:2012-07-25 Published:2012-06-01
Contact: 任力(1973-) ，男，教授，博士生导师，主要从事生物医用材料和组织工程研究． E-mail: psliren@scut．edu．cn E-mail:liuyang_cug@ yahoo.com.cn
About author:刘杨(1985-) ，男，博士生，主要从事高分子材料、生物医用材料研究．
Supported by:
国家自然科学基金重点项目( 50732003; 50803018)

摘要/Abstract

摘要： 采用丙酮沉淀法对海藻酸钠原料进行了提纯，对纯化后的海藻酸钠进行了红外光谱测试和凝胶渗透色谱测试，并测定了提纯前后海藻酸钠样品中剩余蛋白质的含量．此外，通过CaCl₂-海藻酸钠、CaSO₄ /GDL-海藻酸钠和Ca-EDTA/GDL-海藻酸钠3 种交联体系制备了多种海藻酸钙三维多孔支架材料．研究结果表明: 由质量分数为2．5% ～ 3．0%的海藻酸钠所制得的Ca-EDTA/GDL-海藻酸钙三维多孔支架材料中微孔分布均匀，比表面积较大，且具有较好的力学性能，该支架有可能用作组织工程和细胞工程中培养细胞的培养基．

关键词: 组织工程, 多孔支架, 海藻酸钙, 海藻酸钠

Abstract:

Sodium alginate ( AlgNa) was purified via the acetone precipitation,and the product was tested by means of FT-IR and GPC. Then,the contants of residual protein in both the unpurified and the purified samples were measured,and several three-dimension porous calcium alginate scaffolds were fabricated through such three crosslinking systems as CaCl₂-AlgNa,CaSO₄ /GDL-AlgNa and Ca-EDTA/GDL-AlgNa. The results indicate that the
porous Ca-EDTA/GDL-AlgNa scaffold with a sodium alginate content of 2.5%～ 3.0% possesses uniform micropore distribution,large specific surface area and excellent mechanical behavior,which means that it is suitable for the cell culture in tissue engineering and cell engineering.

Key words: tissue engineering, porous scaffold, calcium alginate, sodium alginate

中图分类号:

TQ050.4+25

刘杨任力季培红王迎军. 海藻酸钠的提纯及海藻酸钙多孔支架的制备[J]. 华南理工大学学报(自然科学版), 2012, 40(7): 142-147.

Liu Yang Ren Li Ji Pei-hong Wang Ying-jun. Purification of Sodium Alginate and Preparation of Porous Calcium Alginate Scaffolds[J]. Journal of South China University of Technology(Natural Science Edition), 2012, 40(7): 142-147.

[1]	黄立新, 王占全, 尹寿伟, 等. 海藻酸钠用于红糖溶液脱钙的试验研究[J]. 华南理工大学学报（自然科学版）, 2021, 49(3): 106-113.
[2]	王飞王妍程律莎谢木源张丽君梁世中. hMSCs成骨定向分化及其与PLGA/TCP材料的相容性研究[J]. 华南理工大学学报（自然科学版）, 2014, 42(11): 143-148.
[3]	袁毅桦雷莉何慧贾德民. 环氧氯丙烷交联壳聚糖/海藻酸钠吸附铜离子的研究[J]. 华南理工大学学报(自然科学版), 2012, 40(7): 148-154.
[4]	叶建东罗方聪. 造孔粒子形貌对磷酸钙骨水泥支架材料结构与性能的影响[J]. 华南理工大学学报（自然科学版）, 2010, 38(4): 71-75.
[5]	王雪毓陈玲苏健裕李晓玺余龙. 高直链玉米淀粉对聚己内酯组织工程支架结构和性能的影响[J]. 华南理工大学学报（自然科学版）, 2009, 37(12): 18-22.
[6]	王迎军赵晓飞卢玲任力陈晓峰葛坚刘炳乾. 角膜组织工程支架壳聚糖-胶原复合膜的性能[J]. 华南理工大学学报（自然科学版）, 2006, 34(8): 1-5.