柠檬酸对镧盐转化膜耐蚀性和自愈性的影响

华南理工大学学报(自然科学版) ›› 2012, Vol. 40 ›› Issue (1): 107-113.

柠檬酸对镧盐转化膜耐蚀性和自愈性的影响

孔纲¹ 黄伟¹ 林德鑫² 王霞² 黎汉昌² 卢锦堂¹ 刘玲艳¹

1．华南理工大学材料科学与工程学院，广东广州 510640; 2．广东安恒铁塔钢构有限公司，广东佛山 528000

收稿日期:2011-06-10 修回日期:2011-08-31 出版日期:2012-01-25 发布日期:2011-12-01
通信作者: 孔纲(1971-) ，男，博士，副研究员，主要从事热镀锌及金属表面处理研究． E-mail:konggang@scut.edu.cn
作者简介:孔纲(1971-) ，男，博士，副研究员，主要从事热镀锌及金属表面处理研究．
基金资助:
国际铅锌研究组织项目( ILZRO/IZA/2009023) ; 华南理工大学中央高校基本科研业务费专项资金资助项目( 2009ZM0072)

Effect of Citric Acid on Corrosion Resistance and Self-Healing Ability of Lanthanum Conversion Coating

Kong Gang¹ Huang Wei¹ Lin De-xin² Wang Xia² Li Han-chang² Lu Jin-tang¹ Liu Ling-yan¹

1.School of Materials Science and Engineering,South China University of Technology,Guangzhou 510640,Guangdong,China; 2.Guangdong Anthen Iron Tower and Steel Structure Co. ,Ltd. ,Foshan 528000,Guangdong,China

Received:2011-06-10 Revised:2011-08-31 Online:2012-01-25 Published:2011-12-01
Contact: 孔纲(1971-) ，男，博士，副研究员，主要从事热镀锌及金属表面处理研究． E-mail:konggang@scut.edu.cn
About author:孔纲(1971-) ，男，博士，副研究员，主要从事热镀锌及金属表面处理研究．
Supported by:
国际铅锌研究组织项目( ILZRO/IZA/2009023) ; 华南理工大学中央高校基本科研业务费专项资金资助项目( 2009ZM0072)

摘要/Abstract

摘要： 将热镀锌钢分别浸入添加和不添加柠檬酸的镧盐钝化液中，在镀锌钢表面获得柠檬酸改进型镧盐转化膜和常规镧盐转化膜．用中性盐雾( NSS) 试验、塔菲尔极化和电化学阻抗谱研究了这些试样的耐蚀性能，并对带划痕的柠檬酸改进型和常规镧盐膜层试样进行NSS 腐蚀，用扫描电子显微镜和能谱仪观察分析了腐蚀过程中划痕表面的组织形貌和化学成分．结果表明: 柠檬酸的加入显著提高了镧盐转化膜的耐蚀性能，并使膜层具备自愈性; 腐蚀过程中，划痕附近的柠檬酸镧溶解产生La³⁺ 和柠檬酸根离子，从膜层中扩散迁移至划痕处，形成新的由Zn、O、La、C 元素组成的保护膜，从而抑制了划痕处锌的腐蚀．

关键词: 热镀锌层, 镧盐转化膜, 柠檬酸, 耐蚀性, 自愈性

Abstract:

In this paper,first,hot-dip galvanized steels were immersed into passivation lanthanum solutions with or without citric acid to respectively obtain an improved lanthanum conversion coating or a traditional lanthanum conversion
coating on the steel surface. Next,the corrosion resistances of the two kinds of coatings were investigated via the neutral salt spray ( NSS) test,the Tafel polarization and the electrochemical impedance spectroscopy. Then,the coatings scratched with a knife edge were corroded in a NSS chamber. Finally,the microstructure and chemical composition of the scratch surface during the corrosion were analyzed by means of SEM and EDS. The results
show that the addition of citric acid in the passivation solution remarkably improves the corrosion resistance and the self-healing ability of the coating,and that,during the corrosion,lanthanum ions and citric acid anions produced by the dissolution of LaCit₃ at the scratch migrate from the coating to the scratch to form a new passive coating containing Zn,O,La and C,thus effectively suppressing the corrosion of zinc at the scratch.

Key words: hot-dip galvanizing, lanthanum conversion coating, citric acid, corrosion resistance, self-healing ability

中图分类号:

TG174.4

孔纲黄伟林德鑫王霞黎汉昌卢锦堂刘玲艳. 柠檬酸对镧盐转化膜耐蚀性和自愈性的影响[J]. 华南理工大学学报(自然科学版), 2012, 40(1): 107-113.

Kong Gang Huang Wei Lin De-xin Wang Xia Li Han-chang Lu Jin-tang Liu Ling-yan. Effect of Citric Acid on Corrosion Resistance and Self-Healing Ability of Lanthanum Conversion Coating[J]. Journal of South China University of Technology(Natural Science Edition), 2012, 40(1): 107-113.

[1]	乔丽英姚艳王勇赖宁王维朗. 纯镁表面聚多巴胺膜的制备及表征[J]. 华南理工大学学报（自然科学版）, 2018, 46(7): 16-23.
[2]	赵作福齐锦刚王建中刘兴江王家毅. 电脉冲处理对硅黄铜耐蚀性能的影响[J]. 华南理工大学学报（自然科学版）, 2015, 43(7): 28-32,67.
[3]	左茜李文芳穆松林. 常温下添加剂对有色Ti-Zr转化膜形貌与性能的影响[J]. 华南理工大学学报（自然科学版）, 2014, 42(10): 7-13.
[4]	梁金明唐荻武会宾张鹏程柳伟毛红艳刘晓童. 含Cr 低合金钢在货油舱下底板环境中的腐蚀行为[J]. 华南理工大学学报（自然科学版）, 2013, 41(10): 72-78,91.
[5]	易爱华李文芳杜军穆松林刘宁华. 铝合金表面有色钛/锆转化膜的成膜机理及性能[J]. 华南理工大学学报(自然科学版), 2012, 40(1): 101-106,124.
[6]	袁文辉梁杰李莉. 锆酸锂的制备、表征及吸附CO2的模拟[J]. 华南理工大学学报（自然科学版）, 2011, 39(1): 48-52,62.
[7]	张军军李文芳杜军. 常温时添加剂对Ce-Mn转化膜的影响[J]. 华南理工大学学报（自然科学版）, 2010, 38(4): 76-82.
[8]	卢锦堂张双红孔纲车淳山. 镀锌钢上钼酸盐／硅烷复合膜的组成与耐蚀性[J]. 华南理工大学学报（自然科学版）, 2009, 37(12): 12-17.
[9]	袁文辉王婵月阎慧静李莉 . CO₂吸附剂掺钾锆酸锂的制备及性能表征[J]. 华南理工大学学报（自然科学版）, 2008, 36(7): 26-31.
[10]	许乔瑜桂艳卢锦堂孔纲车淳山 . 热浸Zn—Ti合金镀层的显微组织与耐蚀性能[J]. 华南理工大学学报（自然科学版）, 2008, 36(7): 82-86.
[11]	李浩宋慧宇廖世军. 柠檬酸钠对有机溶胶法制备钴纳米粒子的影响[J]. 华南理工大学学报（自然科学版）, 2008, 36(3): 50-54.
[12]	石林李孟飞兰惠生耿曼. 柠檬酸钠法烟气脱硫技术中硫酸钠的生成控制[J]. 华南理工大学学报（自然科学版）, 2007, 35(6): 111-115.
[13]	熊玲胡永俊徐建蒙继龙. 奥氏体不锈钢的氮、铬离子淹没离子轰击处理[J]. 华南理工大学学报（自然科学版）, 2007, 35(3): 28-32.
[14]	杜军陈东初李文芳张永君彭继华. 铝合金微弧氧化陶瓷膜的微观结构和耐蚀性[J]. 华南理工大学学报（自然科学版）, 2007, 35(3): 6-10.