Optimization of Plasma Electrolytic Oxidation Process and Corrosion Resistance of Oxide Coatings

Chen Li Peng Jia-zhi Yan Zong-cheng Wang Hong-lin Wang Li

School of Chemistry and Chemical Engineering, South China University of Technology, Guangzhou 510640, Guangdong, China

Received:2009-01-20 Revised:2009-03-05 Online:2009-12-25 Published:2009-12-25
Contact: 陈砺（1958-），男，教授，博士牛导师，主要从事绿色化学与可再生资源研究． E-mail:celichen@mail．scut．edu．cn
About author:陈砺（1958-），男，教授，博士牛导师，主要从事绿色化学与可再生资源研究．
Supported by:
广东省科技计划项目（2005850101001）

摘要/Abstract

摘要： 为优化AZ31镁合金的等离子体电解氧化工艺，并对制得的陶瓷膜的耐腐蚀性能进行电化学动力学研究．利用四因素（Na₂SiO₃浓度、KOH浓度、电解氧化电压和电解氧化时间）、三水平的田口方法优化工艺条件，并采用动电位极化曲线扫描评价AZ31镁合金等离子体电解氧化陶瓷膜的耐腐蚀性能．结果表明：该陶瓷膜的耐腐蚀性能受田口正交矩阵中各水平的影响显著，KOH质量浓度对耐腐蚀性能的影响最大；耐腐蚀性能的最优实验参数为：Na₂SiO₃质量浓度20g/L，KOH质量浓度4g/L，电解氧化电压300V和电解氧化时间40min．

关键词: 等离子体电解氧化, 田口方法, 陶瓷膜, AZ31镁合金

Abstract:

:In order to optimize the plasma electrolytic oxidation （PEO） process of AZ31 magnesium alloy and investigate the corrosion resistance of the prepared ceramic coatings in terms of electrochemical kinetics, the Taguchi method was used to perform an orthogonal test in terms of four factors （namely, Na2SiO3 concentration, KOH concentration, electrolytic oxidation voltage and time） and three levels, and the corrosion resistance of the PEO ceramic coatings was evaluated by scanning the potentiodynamic polarization curve. It is found that the three levels in the Taguchi orthogonal array all significantly influence the corrosion resistance, and KOH mass concentration is a major affecting factor; and that, when the PEO is performed with 20g/L Na2SiO3 and 4g/L KOH at 300 V for 40rain, the ceramic coatings are of the highest corrosion resistance.

Key words: plasma electrolytic oxidation, Taguchi method, ceramic coating, AZ31 magnesium alloy

陈砺彭家志严宗诚王红林王丽. 镁合金的等离子体电解氧化工艺优化及膜的耐腐蚀性[J]. 华南理工大学学报（自然科学版）, 2009, 37(12): 49-52.

Chen Li Peng Jia-zhi Yan Zong-cheng Wang Hong-lin Wang Li. Optimization of Plasma Electrolytic Oxidation Process and Corrosion Resistance of Oxide Coatings[J]. Journal of South China University of Technology (Natural Science Edition), 2009, 37(12): 49-52.

[1]	范小江雷颖张锡辉巢猛野口宽. 半程混凝/臭氧化/陶瓷膜过滤新型净水集成工艺[J]. 华南理工大学学报（自然科学版）, 2014, 42(5): 54-59.
[2]	袁文辉罗仡科李莉. 钙饮矿型La_{0. 1}Sr_0.9 CO_0.9 F e₀.₁ O_3-δ膜的非化学计量及氧渗透模型[J]. 华南理工大学学报（自然科学版）, 2007, 35(4): 16-19.
[3]	杜军陈东初李文芳张永君彭继华. 铝合金微弧氧化陶瓷膜的微观结构和耐蚀性[J]. 华南理工大学学报（自然科学版）, 2007, 35(3): 6-10.