23-8N 气门钢的高温摩擦磨损特性

屈盛官尹联民赖福强肖传伟李小强

华南理工大学机械与汽车工程学院，广东广州 510640

收稿日期:2017-04-13 修回日期:2017-05-17 出版日期:2017-12-25 发布日期:2017-10-31
通信作者: 屈盛官(1966-)，男，教授，博士生导师，主要从事金属材料制备成形技术研究． E-mail:qusg@scut.edu.cn
作者简介:屈盛官(1966-)，男，教授，博士生导师，主要从事金属材料制备成形技术研究．
基金资助:
国家自然科学基金资助项目(41572362);广东省科技计划项目(2016B090926001)

High Temperature Friction and Wear Characteristics of 23-8N Valve Steel

QU Sheng-guan YIN Lian-min LAI Fu-qiang XIAO Chuan-wei LI Xiao-qiang

School of Mechanical and Automotive Engineering,South China University of Technology,Guangzhou 510640,Guangdong,China

Received:2017-04-13 Revised:2017-05-17 Online:2017-12-25 Published:2017-10-31
Contact: 屈盛官(1966-)，男，教授，博士生导师，主要从事金属材料制备成形技术研究． E-mail:qusg@scut.edu.cn
About author:屈盛官(1966-)，男，教授，博士生导师，主要从事金属材料制备成形技术研究．
Supported by:
Supported by the National Natural Science Foundation of China(41572362) and the Science and Technology Planning Projects of Guangdong Province(2016B090926001)

摘要/Abstract

摘要： 研究了 23-8N 气门钢采用完全时效和固溶 + 时效热处理后的高温摩擦磨损性能，并对其金相组织、物相组成等进行了分析．结果表明: 随着温度的升高，两种不同热处理试样的摩擦系数和磨损体积均呈现出先减小后增大的趋势; 常温下，完全时效处理试样耐磨性较好，试样表面出现了犁沟和片状磨屑，表现为磨粒磨损和黏着磨损; 而高温时，由于固溶时效处理试样的表面氧化膜更厚，其耐磨损性能更好; 在 400 ℃时，两种试样表面被致密的氧化膜覆盖，所以其磨损量最小，该温度下试样的磨损形式以轻微的氧化磨损为主; 在 500 ～650℃时，随着温度的升高，试样的磨损量逐渐增加，磨损机制也发生转变，由轻微氧化磨损转变为严重磨粒磨损、黏着磨损和氧化膜的疲劳剥落．

关键词: 热处理, 23-8N气门钢, 高温摩擦磨损, 磨损机理

Abstract: In this paper,the high temperature friction and wear characteristics of 23-8N valve steel after full aging and solid solution aging are investigated,and the microstructure and phase composition of the valve steel are also analyzed.The results show that (1) the friction coefficients and wear loss of two different heat treatment specimens both tend to decrease first and then increase with the rising of temperature; (2) at the room temperature,the full aging specimen has better anti-wear performance,and the surfaces of the two different heat treatment specimens are distributed with grooves and adhesive traces,indicating that the prevailed wear mechanism is abrasive wear and ad- hesive wear; (3) at a high temperature,the solution and aging specimen has better wear resistance due to its thic- ker oxide film; (4) at 400℃,the two specimens are covered with dense oxide films,so the wear loss of the speci- mens is the lowest and the main wear mechanism is mild oxidation wear; and (5) as the temperature rises from 500℃ to 650℃,the wear loss gradually increases,and the predominant wear mechanism transforms from mild oxi- dation wear into severe abrasive wear,adhesive wear and the fatigue delamination of oxide films.

Key words: heat treatment, 23-8N engine valve steel, high temperature friction and wear, wear mechanisms

中图分类号:

TH117.1

屈盛官尹联民赖福强肖传伟李小强. 23-8N 气门钢的高温摩擦磨损特性[J]. 华南理工大学学报(自然科学版), 2017, 45(12): 78-84,2.

QU Sheng-guan YIN Lian-min LAI Fu-qiang XIAO Chuan-wei LI Xiao-qiang. High Temperature Friction and Wear Characteristics of 23-8N Valve Steel[J]. Journal of South China University of Technology(Natural Science Edition), 2017, 45(12): 78-84,2.

[1]	夏琴香, 谢章雄, 陈灿, 等. 30CrMnSiA薄壁杯形件的强韧化工艺方法[J]. 华南理工大学学报(自然科学版), 2023, 51(1): 1-7.
[2]	高群玉, 刘强, 董诗婷. 湿热处理对马铃薯淀粉Ghost理化性质的影响[J]. 华南理工大学学报(自然科学版), 2022, 50(8): 12-20.
[3]	陈瑾, 何大伟, 陈玲. 湿热处理环境下咖啡酸/绿原酸对板栗淀粉消化和回生性能的影响[J]. 华南理工大学学报(自然科学版), 2022, 50(8): 41-48.
[4]	吝章国陈家泳唐荻江海涛段晓鸽. 基于层错能的中锰Q&P 钢变形机制研究[J]. 华南理工大学学报（自然科学版）, 2016, 44(2): 140-146.
[5]	扶雄张明朱思明黄强. 湿热处理对玉米淀粉理化性质及消化性的影响[J]. 华南理工大学学报（自然科学版）, 2015, 43(2): 27-32,65.
[6]	端强阎军朱国辉蔡庆伍. 冷速对X80管线钢淬火组织和应变硬化特性的影响[J]. 华南理工大学学报（自然科学版）, 2014, 42(10): 31-35,43.
[7]	袁军平李卫. 饰用BZn10-25镍白铜的镍释放率[J]. 华南理工大学学报（自然科学版）, 2013, 41(2): 141-146.
[8]	李辉段路昭米振莉赵征志唐荻. 双相钢中残留奥氏体的分布及演变规律[J]. 华南理工大学学报（自然科学版）, 2013, 41(10): 92-96.
[9]	陆龙生刘晓辰邓大祥. 多孔壁面沟槽犁切-热处理成形机理[J]. 华南理工大学学报(自然科学版), 2012, 40(1): 35-39,57.
[10]	高群玉武俊超李素玲. 湿热处理对不同直链含量的玉米淀粉性质的影响[J]. 华南理工大学学报（自然科学版）, 2011, 39(9): 1-6.
[11]	苏达根付文祥钟明峰. 太阳光反射材料NaZnPO₄的制备与性能[J]. 华南理工大学学报（自然科学版）, 2011, 39(11): 104-108.
[12]	陆裕东王歆庄志强刘勇. 热处理对BaPbO₃ 薄膜化学组成及薄膜电阻的影响[J]. 华南理工大学学报(自然科学版), 2007, 35(8): 89-92.
[13]	Upul Marapana 江波 Yoshinori Mine. 热处理后蛋白质及MTGase 对猪肉糜凝胶特性的影响[J]. 华南理工大学学报（自然科学版）, 2007, 35(4): 127-133.
[14]	彭俊彪兰林锋杨开霞牛巧丽曹镛. Ta₂O₅的氢热处理对有机薄膜晶体管性能的影响[J]. 华南理工大学学报（自然科学版）, 2006, 34(10): 105-108,112.
[15]	陈明洁沈辉. 热处理下光电致变色器件的结构和变色性能[J]. 华南理工大学学报(自然科学版), 2004, 32(6): 31-35.

23-8N 气门钢的高温摩擦磨损特性

High Temperature Friction and Wear Characteristics of 23-8N Valve Steel

PDF

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价