锰掺杂对铁酸铋结构和磁性的影响

doi:10.3969/j.issn.1000-565X.2013.08.023

华南理工大学学报（自然科学版） ›› 2013, Vol. 41 ›› Issue (8): 139-144.doi: 10.3969/j.issn.1000-565X.2013.08.023

• 物理 • 上一篇

锰掺杂对铁酸铋结构和磁性的影响

陈熹¹何永厚¹陈龙胜²

1．华南理工大学理学院，广东广州 510640; 2．华南理工大学材料科学与工程学院，广东广州 51064

收稿日期:2013-03-25 修回日期:2013-04-27 出版日期:2013-08-25 发布日期:2013-07-01
通信作者: 陈熹(1972-)，男，教授，博士生导师，主要从事凝聚态物理研究． E-mail:xichen@scut.edu.cn
作者简介:陈熹(1972-)，男，教授，博士生导师，主要从事凝聚态物理研究．
基金资助:
国家自然科学基金资助项目(11174082);华南理工大学中央高校基本科研业务费专项资金资助项目(2012ZZ0078)

Effects of Mn Doping on Structure and Magnetic Properties of Bismuth Ferrite

Chen Xi¹He Yong- hou¹Chen Long- sheng²

1.School of Science,South China University of Technology,Guangzhou 510640,Guangdong,China;2.School of Materials Science and Engineering,South China University of Technology,Guangzhou 510640,Guangdong,China

Received:2013-03-25 Revised:2013-04-27 Online:2013-08-25 Published:2013-07-01
Contact: 陈熹(1972-)，男，教授，博士生导师，主要从事凝聚态物理研究． E-mail:xichen@scut.edu.cn
About author:陈熹(1972-)，男，教授，博士生导师，主要从事凝聚态物理研究．
Supported by:
国家自然科学基金资助项目(11174082);华南理工大学中央高校基本科研业务费专项资金资助项目(2012ZZ0078)

摘要/Abstract

摘要： 用溶胶凝胶法制备了BiFe_1－xMn_xO₃( 0≤ x ≤0．3) 系列粉晶样品，并研究了Mn 掺杂对其结构和磁性的影响．XRD 和拉曼光谱分析表明 Mn 掺杂使 BiFeO₃ 的晶体结构和振动模式发生了变化．Rietveld 精修结果显示，在掺杂量 x =0．1 附近，BiFeO₃ 的晶体结构从菱方R3c 相转变为正交 Pbnm 相．对样品的磁性测量表明，随着 Mn 掺杂量的增加，样品的剩余磁化强度逐渐增大，在相变点附近达到最大值．这种磁性的变化与 Mn 掺杂导致的晶体结构变化有很强的关联，表明 Dzyaloshinskii- Moriya 相互作用是 BiFe_1－xMn_xO₃ 磁性增强的主要原因．

关键词: 多重铁材料, Rietveld 精修, 磁性

Abstract:

BiFe_1－xMn_xO₃( 0≤ x ≤0.3) crystal powders were synthesized via the sol- gel method,and the effects of Mn doping on the structure and magnetic properties of the product were investigated.XRD and Raman spectroscopy analyses reveal that Mn doping changes the crystal structure and vibration mode of BiFeO₃.Rietveld refinement re-sults indicate that the substitution of Mn at Fe- site brings about a structural phase transition from the rhombohedral R3c to the orthorhombic Pbnm around x =0.1.Magnetic measurement results demonstrate that,with the increase of the Mn dosage x,the remanent magnetization gradually increases and reaches its maximum near the phase transition point.In addition,the enhanced magnetization of BiFe_1－xMn_xO₃ strongly correlates with the variations of the crystal structural,which indicates that it is mainly attributed to the Dzyaloshinskii- Moriya interaction.

Key words: multiferroic material, rietveld refinement, magnetic property

中图分类号:

陈熹何永厚陈龙胜. 锰掺杂对铁酸铋结构和磁性的影响[J]. 华南理工大学学报（自然科学版）, 2013, 41(8): 139-144.

Chen Xi He Yong- hou Chen Long- sheng. Effects of Mn Doping on Structure and Magnetic Properties of Bismuth Ferrite[J]. Journal of South China University of Technology (Natural Science Edition), 2013, 41(8): 139-144.

[1]	朱军田宗军刘志东沈理达黄因慧王桂峰. 摩擦辅助喷射电沉积制备纳米晶光亮镍[J]. 华南理工大学学报（自然科学版）, 2011, 39(11): 92-97.
[2]	唐爱民张宏伟陈港田英姿刘映尧. 磁性纳米复合纤维及磁性纸的制备与性能[J]. 华南理工大学学报（自然科学版）, 2009, 37(3): 75-80.

锰掺杂对铁酸铋结构和磁性的影响

Effects of Mn Doping on Structure and Magnetic Properties of Bismuth Ferrite

PDF

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 2

编辑推荐

Metrics

本文评价