电应力对Al /SnAgCu /Cu 互连结构剪切强度及断裂模式的影响

华南理工大学学报(自然科学版) ›› 2011, Vol. 39 ›› Issue (11): 120-124.

电应力对Al /SnAgCu /Cu 互连结构剪切强度及断裂模式的影响

陆裕东¹万明²恩云飞¹王歆²成俊³何小琦¹

1．工业和信息化部电子第五研究所，广东广州 510610; 2．华南理工大学材料科学与工程学院，广东广州 510640; 3．华南理工大学电子与信息学院，广东广州 510640

收稿日期:2011-01-11 修回日期:2011-07-25 出版日期:2011-11-25 发布日期:2011-10-03
通信作者: 陆裕东(1979-) ，男，博士，副研究员，主要从事微电子封装与可靠性研究． E-mail:yudonglu@yahoo.com.cn
作者简介:陆裕东(1979-) ，男，博士，副研究员，主要从事微电子封装与可靠性研究．
基金资助:
科技部国际科技合作与交流重大项目( 2010DFB10070) ; 国家预研基金资助项目( 51323060305) ; 中国博士后科学基金资助项目( 20080430825)

Effect of Current Stress on Shear Strength and Fracture Mode of Al /SnAgCu /Cu Interconnecting Structure

Lu Yu-dong¹Wan Ming²En Yun-fei¹Wang Xin²Cheng Jun³He Xiao-qi¹

1. The 5th Electronics Research Institute of the Ministry of Industry and Information Technology,Guangzhou 510610,Guangdong,China; 2. School of Materials Science and Engineering,South China University of Technology,Guangzhou 510640,Guangdong,China; 3. School of Electronic and Information Engineering,South China University of Technology,Guangzhou 510640,Guangdong，China

Received:2011-01-11 Revised:2011-07-25 Online:2011-11-25 Published:2011-10-03
Contact: 陆裕东(1979-) ，男，博士，副研究员，主要从事微电子封装与可靠性研究． E-mail:yudonglu@yahoo.com.cn
About author:陆裕东(1979-) ，男，博士，副研究员，主要从事微电子封装与可靠性研究．
Supported by:
科技部国际科技合作与交流重大项目( 2010DFB10070) ; 国家预研基金资助项目( 51323060305) ; 中国博士后科学基金资助项目( 20080430825)

摘要/Abstract

摘要： 连结构的剪切失效位置和失效模式，分析了两种不同应力条件下互连结构失效形貌间的差异，研究并确定了高电流应力导致的电迁移对Al /SnAgCu /Cu 互连结构剪切强度及断裂模式的影响．结果表明: 高温老化实验后，倒装凸点互连结构中出现Al 金属/焊料界面的脆性开裂和凸点焊料的延展性断裂两种剪切断裂模式; 高温高电流应力条件下老化后，倒装凸点互连结构的剪切失效位置和断面形貌发生变化，电迁移作用导致的层状空洞和金属间化合物的异常生长成为影响倒装凸点互连结构剪切强度及失效模式的主要因素; 同时，由于倒装凸点串联回路中电流方向的交替性变化，倒装凸点互连结构在加电实验中出现的两种断裂模式在回路中呈交替分布的特殊失效现象．

关键词: SnAgCu, 凸点, 互连结构, 机械强度, 断裂模式, 金属间化合物, 电迁移

Abstract:

The failure position and failure mode of SnAgCu flip-chip solder bumps enduring thermal stress and electrical/thermal complex stress before shear test were investigated,and the difference in microstructure of the interconnecting structure enduring different stresses were compared. Moreover,the effects of electromigration induced by high current density on the shear strength and the fracture mode of Al /SnAgCu /Cu interconnecting structure were analyzed. The results indicate that there are two shear fracture modes of the flip-chip solar bumps after the aging at a high temperature,namely the brittle fracture on the Al-solder interface and the ductile fracture in the solder bumps,that the failure position and the fracture surface morphology of the interconnecting structure change after the aging at a high temperature and high current stress,that the pancake-type voids and the abnormal growth of intermetallic compound induced by electromigration are the main cause of failure,and that the two fracture modes alternately distribute in the interconnecting structure due to the alternate change of current flow in flip-chip solder bumps.

Key words: SnAgCu, bump, interconnecting structure, mechanical strength, fracture mode, intermetallic compound, electromigration

中图分类号:

TG401
TG111

陆裕东万明恩云飞王歆成俊何小琦. 电应力对Al /SnAgCu /Cu 互连结构剪切强度及断裂模式的影响[J]. 华南理工大学学报(自然科学版), 2011, 39(11): 120-124.

Lu Yu-dong Wan Ming En Yun-fei Wang Xin Cheng Jun He Xiao-qi. Effect of Current Stress on Shear Strength and Fracture Mode of Al /SnAgCu /Cu Interconnecting Structure[J]. Journal of South China University of Technology(Natural Science Edition), 2011, 39(11): 120-124.

[1]	林晓玲章晓文高汭. 一种倒装芯片 /多层互连结构封装 IC 的修改方法 [J]. 华南理工大学学报（自然科学版）, 2020, 48(12): 63-71.
[2]	周斌李勋平恩云飞卢桃何小琦姚若河. 高温时效下 Sn/SnPb 混装焊点的微观组织研究[J]. 华南理工大学学报（自然科学版）, 2016, 44(5): 8-14.
[3]	金雪莉曾令可李萍侯来广. 聚丙烯纤维对吸声性能的影响及其神经网络模拟[J]. 华南理工大学学报（自然科学版）, 2007, 35(12): 97-101.
[4]	詹郁生郑学仁. 集成电路金属互连焦耳热效应的测试与修正[J]. 华南理工大学学报(自然科学版), 2004, 32(5): 34-37.
[5]	方玉堂, 丁静, 范娟, 等. 新型Al³⁺掺杂硅胶吸附材料的制备与性能[J]. 华南理工大学学报(自然科学版), 2004, 32(3): 5-9,19.
[6]	李小强, 李元元, 邵明, 等. 加镍过渡层钛合金/不锈钢网的扩散连接技术[J]. 华南理工大学学报(自然科学版), 2003, 31(6): 51-55.