基于含硒窄带隙聚合物太阳能电池的性能

华南理工大学学报（自然科学版） ›› 2005, Vol. 33 ›› Issue (2): 6-9,18.

基于含硒窄带隙聚合物太阳能电池的性能

田仁玉阳仁强周清梅彭俊彪曹镛

华南理工大学高分子光电材料与器件研究所，广东广州 510640

收稿日期:2004-05-12 出版日期:2005-02-25 发布日期:2005-02-25
通信作者: 彭俊彪，E—mail：psjbpeng@scut．edu．cn E-mail:rytian@scut.edu.cn
作者简介:田仁玉(1971-)，女，讲师，博士生，主要从事高分子光电器件方面的研究．
基金资助:
国家“973”基金资助项目(2002CB613405)；广东省自然科学基金资助项目(990623)

Performances of Photovoitaic Cells Based on Se-Containing Low-Bandgap Polymer

Tian Ren-yu Yang Ren-qiang Zhou Qing-mei Peng Jun-biao Cao Yong

Institute of Polymer Optodectronic Materials and Devices,South China Univ.of Tech.,Guangzhou 510640,Guangdong,China

Received:2004-05-12 Online:2005-02-25 Published:2005-02-25
Contact: 彭俊彪，E—mail：psjbpeng@scut．edu．cn E-mail:rytian@scut.edu.cn
About author:田仁玉(1971-)，女，讲师，博士生，主要从事高分子光电器件方面的研究．
Supported by:
国家“973”基金资助项目(2002CB613405)；广东省自然科学基金资助项目(990623)

摘要/Abstract

摘要： 为扩展聚合物太阳能电池的光谱响应范围，选用含硒窄带隙聚合物—— 聚[2，7-(9，9-二正辛基)芴-5，5’-(4，7-二硒吩-2，2’-基)-2，1，3-苯并硒二唑](PFSeBSe)作电子给体，C60衍生物(PCBM)作电子受体，将二者共混，制备了单活化层聚合物太阳能电池．研究表明，PFSeBSe与PCBM 的最佳混合质量比约为1：4，在Air Mass1．5(100mw•cm^-2 )模拟太阳光源辐照下，用LiF/Al作为阴极，器件的最大能量转换效率为0．423%，光敏响应可扩展到700nm以上，比文献报道的结果红移了30～50nm，表明该体系的吸收与地表太阳光谱能量分布更加匹配．

关键词: 太阳能电池, 含硒窄带隙聚合物, 光敏响应

Abstract:

Se-containing low-bandgap polymer-poly[2,7-(9,9-dioctyl)fluorene-co-5,5’-(4,7-diselenophenyl)-2,2’-v1-2,1,3-benzoselenodiazole](PFSeBSe)was used as the electron donor in order to expand the spectral re-sponse region of polymer photovohaic cells(PPVCs).Single-layer PPVC was made by blending PFSeBSe with C60 derivative(PCBM),the electron acceptor.The results indicate that the optimal blend ratio of PFSeBSe to PCBM is about 1:4 (in mass),and that a maximum power conversion efficiency of 0.423%under Air Mass 1.5 solar simu-lat0r(100 mW•cm^-2 ),can be obtained when LiF/Al is used as the cathode.Th e photosensitivity of the cell ex-pands to more than 700 nm．which is 30 ~50 nm red-shifted compared with the results in the literature,suggesting a better match of the absorption of the blend system to the terrestrial solar spectrum.

Key words: photovohaic cells, Se-containing low-bandgap polymer, photosensitivity

田仁玉阳仁强周清梅彭俊彪曹镛. 基于含硒窄带隙聚合物太阳能电池的性能[J]. 华南理工大学学报（自然科学版）, 2005, 33(2): 6-9,18.

Tian Ren-yu Yang Ren-qiang Zhou Qing-mei Peng Jun-biao Cao Yong. Performances of Photovoitaic Cells Based on Se-Containing Low-Bandgap Polymer[J]. Journal of South China University of Technology (Natural Science Edition), 2005, 33(2): 6-9,18.