大型MA 类钢桥面铺装高温性能加速加载试验研究

doi:10.3969/j.issn.1000-565X.2014.12.004

华南理工大学学报（自然科学版） ›› 2014, Vol. 42 ›› Issue (12): 21-26,34.doi: 10.3969/j.issn.1000-565X.2014.12.004

大型MA 类钢桥面铺装高温性能加速加载试验研究

张肖宁¹ 容洪流^1,2 黄文柯¹ 陈剑华¹

1．华南理工大学土木与交通学院，广东广州 510640; 2．广西大学土木建筑工程学院，广西南宁 530004

收稿日期:2014-01-10 修回日期:2014-09-30 出版日期:2014-12-25 发布日期:2014-11-17
通信作者: 张肖宁(1951-)，男，博士，教授，博士生导师，主要从事沥青路面结构与材料研究． E-mail:prozxn@163.com
作者简介:张肖宁(1951-)，男，博士，教授，博士生导师，主要从事沥青路面结构与材料研究．
基金资助:
国家自然科学基金重点资助项目(51038004);国家重大科技支撑计划项目(2011BAG07B03)

Accelerated Load Testing of High-Temperature Performance of Long-Span MA Steel Bridge Deck Pavement

Zhang Xiao-ning¹ Rong Hong-liu^1,2 Huang Wen-ke¹ Chen Jian-hua¹

1.School of Civil Engineering and Transportation,South China University of Technology,Guangzhou 510640,Guangdong,China;2.College of Civil Engineering and Architecture,Guangxi University,Nanning 530004,Guangxi,China

Received:2014-01-10 Revised:2014-09-30 Online:2014-12-25 Published:2014-11-17
Contact: 张肖宁(1951-)，男，博士，教授，博士生导师，主要从事沥青路面结构与材料研究． E-mail:prozxn@163.com
About author:张肖宁(1951-)，男，博士，教授，博士生导师，主要从事沥青路面结构与材料研究．
Supported by:
国家自然科学基金重点资助项目(51038004);国家重大科技支撑计划项目(2011BAG07B03)

摘要/Abstract

摘要： 高温性能是浇注式沥青混凝土的薄弱环节．采用南非 MLS66 型加速加载设备，对港珠澳大桥拟采用的两种英国体系浇注式沥青(MA)钢桥面铺装结构进行大型直道高温性能加速加载试验．结果表明，用德国 GA 工艺生产的 MA(即 GMA)铺装结构高温性能可以达到甚至略优于英国传统工艺生产的 MA 铺装结构高温性能，采用 GMA 工艺解决了今后实桥桥面铺装施工时的生产工效问题，同时 GMA 浇注式沥青混凝土的性能可以达到英国标准体系要求．

关键词: 浇注式沥青, 钢桥面铺装, 高温性能, 加速加载试验

Abstract:

The mastic asphalt (MA) has a weak high-temperature performance.In the investigation,the high-tem-perature performance of two kinds of British-style MA steel bridge deck pavements to be used in Hong Kong-Zhuhai-Macao Bridge was tested under accelerated load by using MLS66.The results show that (1) the MA produced withGerman-style GA craft,namely GMA,is equivalent or even superior to that produced with the traditional British-style craft in terms of the high-temperature performance; and (2) GMA can solve the real production ergonomicsproblems of bridge deck pavements,and the MA performance can meet the British-style standard.

Key words: mastic asphalt, steel bridge deck pavement, high-temperature performance, accelerated load testing

中图分类号:

张肖宁容洪流黄文柯陈剑华 . 大型MA 类钢桥面铺装高温性能加速加载试验研究[J]. 华南理工大学学报（自然科学版）, 2014, 42(12): 21-26,34.

Zhang Xiao-ning Ｒong Hong-liu Huang Wen-ke Chen Jian-hua . Accelerated Load Testing of High-Temperature Performance of Long-Span MA Steel Bridge Deck Pavement[J]. Journal of South China University of Technology (Natural Science Edition), 2014, 42(12): 21-26,34.

[1]	高俊锋汪海年尤占平陈曦姜鑫. 基于MSCR试验的生物沥青高温性能评价[J]. 华南理工大学学报（自然科学版）, 2017, 45(11): 24-30.
[2]	高俊锋汪海年尤占平陈曦姜鑫. 基于MSCR试验的生物沥青高温性能评价[J]. 华南理工大学学报（自然科学版）, 2017, 45(11): 0-0.
[3]	张肖宁张顺先徐伟黄志勇吴文亮苑苗苗. 基于使用性能的钢桥面铺装环氧沥青混凝土设计[J]. 华南理工大学学报(自然科学版), 2012, 40(7): 1-7.
[4]	王端宜雷超旭蔡旭区仕权. 沥青路面的逆向设计及其试验研究[J]. 华南理工大学学报（自然科学版）, 2010, 38(10): 84-88,110.
[5]	陈俊岳学军黄晓明 . 沥青胶结料的高温性能评价新指标——纯黏性稠度[J]. 华南理工大学学报（自然科学版）, 2008, 36(2): 35-40.
[6]	彭波袁万杰陈忠达. 用车辙系数评价沥青混合料的抗车辙性能[J]. 华南理工大学学报（自然科学版）, 2005, 33(12): 84-86.

大型MA 类钢桥面铺装高温性能加速加载试验研究

Accelerated Load Testing of High-Temperature Performance of Long-Span MA Steel Bridge Deck Pavement

PDF

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 6

编辑推荐

Metrics

本文评价