以水性丙烯酸树脂为基质的低居里点PTC材料

doi:10.12141/j.issn.1000-565X.200656

华南理工大学学报（自然科学版） ›› 2021, Vol. 49 ›› Issue (9): 80-87.doi: 10.12141/j.issn.1000-565X.200656

所属专题： 2021年材料科学与技术

以水性丙烯酸树脂为基质的低居里点PTC材料

李静^1,2 韩淑镁¹ 李文君³ 段诗雨¹

1.华南理工大学化学与化工学院，广东广州 510640；2.华南理工大学珠海现代产业创新研究院，广东珠海 519000；
3.北京空间飞行器总部，北京 100086

收稿日期:2020-11-02 修回日期:2021-01-08 出版日期:2021-09-25 发布日期:2021-09-01
通信作者: 李静（1966-），女，博士，教授，主要从事功能复合材料的研究。 E-mail:ljing@scut.edu.cn
作者简介:李静（1966-），女，博士，教授，主要从事功能复合材料的研究。
基金资助:
国防部科技工业局“十三五”民用航天技术预研项目（A2180150）；广州市科技局基础与应用基础研究项目（B3200390）

PTC Materials with Low Curie Temperature Point Based on Waterborne Acrylic Resin Matrix

LI Jing^1,2HAN Shumei¹LI Wenjun³ DUAN Shiyu¹

1.School of Chemistry and Chemical Engineering，South China University of Technology， Guangzhou 510640，Guangdong，
China；2.SCUT-Zhuhai Modern Industrial Innovation，Zhuhai 519000，Guangdong，China；3.Beijing Institute of Spacecraft
System Engineering，Beijing 100086，China

Received:2020-11-02 Revised:2021-01-08 Online:2021-09-25 Published:2021-09-01
Contact: 李静（1966-），女，博士，教授，主要从事功能复合材料的研究。 E-mail:ljing@scut.edu.cn
About author:李静（1966-），女，博士，教授，主要从事功能复合材料的研究。
Supported by:
Supported by the Civil Space Technology Pre-Research Program During the “13th Five-Year Plan” of the Bureau of Science, Technology and Industry, the Ministry of National Defence (A2180150)

摘要/Abstract

摘要： 具有正温度系数（PTC）的导电高分子复合材料（CPCs）在自控温加热中有很多应用，但现有针对CPCs的研究主要集中在高温区域，鲜见常低温段的报道。文中提出了以水性丙烯酸树脂为基体制备低居里温度点PTC材料的方法，并讨论了控温材料和导电填料配比对材料居里温度的影响。在水性丙烯酸树脂与有机酸晶体的共聚物中加入Ni粉，得到了居里温度点接近有机酸晶体熔点、初始电阻低的PTC材料；通过调节 Ni粉的比例，材料的居里温度点可在一定范围内波动。结果表明：当Ni的质量分数为30％时，材料的初始电阻率可达1.96 Ω·ｃｍ，PTC强度超过6；加热试验后，材料的热容量和电性能经热循环未发生明显变化，具有很强的重复性。

关键词: PTC材料, 导电高分子复合材料, 控温加热, 低居里温度点, PTC效应, PTC强度

Abstract: Conductive polymer composites （CPCs） with positive temperature coefficient （PTC） have many applications in self-regulating heating fields.However，current researches on CPCs are mainly concentrated in the high temperature region，and few reports are concerned on low temperature segment.This study proposed a method of making a low Curie temperature point PTC material with water-based acrylic resin as matrix，and discussed the effects of temperature-controlled materials and different proportions of conductive fillers on Curie temperature.By adding Ni powder into the copolymer of water-borne acrylic resin and organic acid crystal，the PTC materials with low initial resistance and a Curie temperature point near the melting point of organic acid crystal were obtained.The Curie temperature point of the material can be adjusted within a certain range by regulating the proportion of Ni powder.Results show that，when the mass fraction of Ni powder is 30%，the initial resistivity of the material can reach 1.96Ω·cm，and the PTC intensity can exceed 6.Heating test results show that the heating capacity and electrical properties of the materials have no significant change after the thermal cycle，indicating good repeatability.

Key words: PTC materials, conductive polymer composites, temperature-controlled heating, low Curie temperature point, PTC effect, PTC intensity

中图分类号:

TB333

李静, 韩淑镁, 李文君, 等. 以水性丙烯酸树脂为基质的低居里点PTC材料[J]. 华南理工大学学报（自然科学版）, 2021, 49(9): 80-87.

LI Jing, HAN Shumei, LI Wenjun, et al. PTC Materials with Low Curie Temperature Point Based on Waterborne Acrylic Resin Matrix[J]. Journal of South China University of Technology (Natural Science Edition), 2021, 49(9): 80-87.

以水性丙烯酸树脂为基质的低居里点PTC材料

PTC Materials with Low Curie Temperature Point Based on Waterborne Acrylic Resin Matrix

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 1

编辑推荐

Metrics

本文评价