高温喷水冷却后方钢管高强混凝土的界面黏结性能

doi:10.12141/j.issn.1000-565X.190904

华南理工大学学报（自然科学版） ›› 2020, Vol. 48 ›› Issue (9): 20-33.doi: 10.12141/j.issn.1000-565X.190904

高温喷水冷却后方钢管高强混凝土的界面黏结性能

陈宗平^1,2 周济¹ 陈建佳¹ 周星宇¹

1．广西大学土木建筑工程学院，广西南宁 530004;2．广西大学工程防灾与结构安全教育部重点实验室，广西南宁 530004

收稿日期:2019-12-16 修回日期:2020-04-01 出版日期:2020-09-25 发布日期:2020-09-01
通信作者: 陈宗平 (1975-)，男，博士，教授，主要从事钢－混凝土组合结构、再生混凝土结构、海洋及近海混凝土结构研究。 E-mail:zpchen@gxu.edu.cn
作者简介:陈宗平 (1975-)，男，博士，教授，主要从事钢－混凝土组合结构、再生混凝土结构、海洋及近海混凝土结构研究。
基金资助:
国家自然科学基金资助项目 (51268004); 广西自然科学基金重点资助项目 (2016GXNSFDA380032); 八桂学者专项经费资助项目 ( ［2019］ 79 号)

Interface Bond Behavior of High Strength Concrete Filled Square Steel Tube Subjected to High Temperature and Subsequent Water Cooling

CHEN Zongping^1,2 ZHOU Ji¹ CHEN Jianjia¹ ZHOU Xingyu¹

1． College of Civil Engineering and Architecture，Guangxi University，Nanning 530004，Guangxi，China;2． MOE Key Laboratory of Disaster Prevention and Structural Safety，Guangxi University，Nanning 530004，Guangxi，China

Received:2019-12-16 Revised:2020-04-01 Online:2020-09-25 Published:2020-09-01
Contact: 陈宗平 (1975-)，男，博士，教授，主要从事钢－混凝土组合结构、再生混凝土结构、海洋及近海混凝土结构研究。 E-mail:zpchen@gxu.edu.cn
About author:陈宗平 (1975-)，男，博士，教授，主要从事钢－混凝土组合结构、再生混凝土结构、海洋及近海混凝土结构研究。
Supported by:
Supported by the National Natural Science Foundation of China (51268004)，the Key Projects of Guangxi Natu-ral Science Foundation (2016GXNSFDA380032) and the Special Fund Project for “Bagui”Scholars ( ［2019］ No. 79)

摘要/Abstract

摘要： 为研究高温喷水冷却后方钢管高强混凝土界面间的黏结性能，设计 22 个试件进行静力推出试验，其中包括 18 个喷水冷却试件和 4 个自然冷却试件，主要考虑混凝土强度、历经最高温度、锚固长度、恒温时长和冷却方式的影响。通过试验揭示了高温喷水冷却后方钢管高强混凝土界面黏结失效机理，分析了各变化参数对其黏结性能的影响，并提出了高温喷水冷却后方钢管高强混凝土极限黏结强度和残余黏结强度的计算公式。结果表明: 高温喷水冷却后方钢管高强混凝土加载端与自由端的荷载滑移曲线可分为两类典型曲线; 高温喷水冷却后，试件的黏结强度随历经最高温度的升高先增大后减小，随混凝土强度的增大而增大，随锚固长度的增大而减小，且与恒温 60 min 试件相比，恒温90min 试件的黏结强度有所回升; 与自然冷却试件相比，喷水冷却试件的极限黏结强度、残余黏结强度与剪切黏结刚度均较小，但界面耗能能力较大; 运用文中所提出的黏结强度计算公式算得的结果与试验值吻合良好。

关键词: 方钢管, 高强混凝土, 高温喷水冷却, 黏结强度, 滑移性能

Abstract: To study the interface bond behavior of high strength concrete filled square steel tube (HSST) subjected to high temperature and subsequent water cooling，22 specimens were designed to carry out static push-out tests in-cluding 18 water cooling specimens and 4 natural cooling specimens，and the effects of concrete strength，maximum temperature，anchorage length，constant temperature and cooling mode were mainly considered． The interface fai-lure mechanism of the HSST subjected to high temperature and subsequent water cooling was revealed through ex-periments，and the influence of various parameters on the bond properties was analyzed． In addition，the formulas for calculating ultimate bond strength and residual bond strength of HSST subjected to high temperature and subse-quent water cooling were put forward． The results show that the load-slip curves of the loading end and the free end of the specimen subjected to high temperature and subsequent water cooling can be divided into two kinds of typical curves． After high temperature and subsequent water cooling，the bond strength of the specimen increases first and then decreases with the increase of the maximum temperature，increases with the increase of the concrete strength，and decreases with the increase of the anchor length． Compared with that at holding time for 60 min，the bond strength of the specimen at holding time for 90 min rebounds． Compared with the natural cooling specimens，the ul-timate bond strength，residual bond strength and bond shear stiffness of the specimens subjected to water cooling are smaller，and the interface energy dissipation capacity is larger． The results calculated by the calculation formula of the bond strength proposed agrees well with the experimental results．

Key words: square steel tube, high strength concrete, high temperature and subsequent water cooling, bond strength, slipping behavior

中图分类号:

TU398

陈宗平, 周济, 陈建佳, 等. 高温喷水冷却后方钢管高强混凝土的界面黏结性能[J]. 华南理工大学学报（自然科学版）, 2020, 48(9): 20-33.

CHEN Zongping, ZHOU Ji, CHEN Jianjia, et al. Interface Bond Behavior of High Strength Concrete Filled Square Steel Tube Subjected to High Temperature and Subsequent Water Cooling[J]. Journal of South China University of Technology (Natural Science Edition), 2020, 48(9): 20-33.

[1]	马煜东, 马恺泽, 魏慧, 等. 掺入不同尺寸钢纤维的高强混凝土深梁抗剪性能[J]. 华南理工大学学报（自然科学版）, 2021, 49(4): 20-27,38.
[2]	常鸿飞, 左文康, 任腾龙, 等. 表面焊板加强方钢管 T 型节点的受压性能[J]. 华南理工大学学报（自然科学版）, 2019, 47(11): 113-121,139.
[3]	洪雷朵润民王苏岩. 粘结长度对CFRP-C60 混凝土界面性能的影响[J]. 华南理工大学学报（自然科学版）, 2016, 44(2): 14-19.
[4]	孟刚贾金青高军程叶浩. 预应力钢骨超高强混凝土梁裂缝宽度试验与计算[J]. 华南理工大学学报（自然科学版）, 2014, 42(10): 102-109,116.
[5]	常鸿飞夏军武常虹俞广东. 方钢管覆板加强 T 型节点的受压承载机理[J]. 华南理工大学学报（自然科学版）, 2013, 41(6): 77-83.
[6]	郑顺潮黄培彦郭馨艳郑小红周昊. 钢纤维聚合物高强混凝土的温度疲劳性能[J]. 华南理工大学学报（自然科学版）, 2011, 39(9): 88-92.
[7]	吴波李杰黄玉龙王帆 . 不同饰面材料高强混凝土柱的耐火性能[J]. 华南理工大学学报（自然科学版）, 2009, 37(3): 120-126,131.
[8]	张耀春郜京峰姚淇誉王海明. 薄壁设肋方钢管混凝土柱穿心高强螺栓的抗剪性能[J]. 华南理工大学学报（自然科学版）, 2009, 37(12): 111-117.
[9]	巴恒静苏安双高小建陶琦. 单面干燥条件下受约束高强混凝土的早期开裂研究[J]. 华南理工大学学报（自然科学版）, 2008, 36(1): 110-116.
[10]	吴波洪洲. 钢筋混凝土简支梁的耐火极限[J]. 华南理工大学学报（自然科学版）, 2006, 34(7): 82-87.
[11]	吴波洪洲. 高强混凝土柱的耐火极限[J]. 华南理工大学学报（自然科学版）, 2006, 34(11): 64-69.

高温喷水冷却后方钢管高强混凝土的界面黏结性能

Interface Bond Behavior of High Strength Concrete Filled Square Steel Tube Subjected to High Temperature and Subsequent Water Cooling

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 11

编辑推荐

Metrics

本文评价