Control of Shape Deviation for Multi-Point Stretch Bending Profiles

LIANG Ji-cai¹ LI Yi²

1.Roll Forging Institute,Jilin University,Changchun 130025,Jilin,China; 2.College of Materials Science and Engineering,Jilin University,Changchun 130025,Jilin,China

Received:2015-08-24 Revised:2016-03-29 Online:2016-07-25 Published:2016-06-05
Contact: 李义(1974-)，男，博士，教授，主要从事材料加工研究． E-mail:henrylee@jlu.edu.cn
About author:梁继才(1960-)，男，博士，教授，主要从事材料加工研究． E-mail:liangjicai@126． com
Supported by:
Supported by the Project of Special Industry Base Construction of Jilin Province(20130302010GX)

摘要/Abstract

摘要： 首先阐述了型材无模多点拉弯成形的基本原理，分析了多点拉弯成形中形状偏差和表面压痕缺陷的形成机理以及影响因素;然后针对传统的模具型面补偿优化的局限性，提出了控制形状偏差和表面压痕缺陷的模具型面优化设计方法，并建立了多点拉弯成形模具型面迭代模型;最后以某铝型材为研究对象，进行了模具型面迭代优化试验研究．结果表明:模具型面形状及位置经过迭代优化后，形状偏差量明显降低(最大形状偏差量从 2． 32mm 降低至 0． 61mm)，表面压痕缺陷得到有效抑制．

关键词: 型材, 多点拉弯成形, 模具型面, 迭代优化, 形状偏差

Abstract: Firstly,the basic formation principle of multi-point stretch bending profiles was expounded,and the cau- ses as well as the influence factors of shape deviation and surface indentation defect for multi-point stretch bending profiles were analyzed.Secondly,by taking into consideration the limitations of conventional profile compensation optimization methods,a new optimization method to control shape deviation and avoid indentation defect was pro- posed.Then,an iterative model of multi-point stretch bending profiles was constructed.Finally,some experiments were carried out to verify the effectiveness of the proposed model.The results indicate that,after the iterative opti- mization of die shape and location,the shape deviation decreases greatly from the maximum 2.32mm to 0.61mm,and the surface indentation defect is controlled effectively.

Key words: profile, multi-point stretch bending, die shape, iterative optimization, shape deviation

中图分类号:

TG156

梁继才李义. 型材多点拉弯成形制件的形状偏差控制[J]. 华南理工大学学报（自然科学版）, 2016, 44(7): 29-33.

LIANG Ji-cai LI Yi . Control of Shape Deviation for Multi-Point Stretch Bending Profiles[J]. Journal of South China University of Technology (Natural Science Edition), 2016, 44(7): 29-33.

[1]	李义梁策于佳奇梁继才陈广义. 管材多点柔性拉弯成形制件形状误差研究[J]. 华南理工大学学报（自然科学版）, 2018, 46(7): 24-29.
[2]	梁策赵宏伟李义梁继才. 型材多点柔性成型模具头体的调形方法[J]. 华南理工大学学报（自然科学版）, 2017, 45(9): 142-146.
[3]	滕菲梁继才张万喜王雪高嵩. 矩形截面型材三维拉弯成形的回弹预测[J]. 华南理工大学学报（自然科学版）, 2015, 43(2): 107-113.
[4]	梁继才滕菲高嵩陈广义魏志勇. 矩形铝型材柔性三维拉弯工艺的多目标优化[J]. 华南理工大学学报（自然科学版）, 2013, 41(9): 143-148.
[5]	陈永松周少奇. 铝型材厂工业污泥中重金属的含量及浸出特性[J]. 华南理工大学学报（自然科学版）, 2008, 36(12): 70-74,84.

型材多点拉弯成形制件的形状偏差控制

Control of Shape Deviation for Multi-Point Stretch Bending Profiles

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 5

编辑推荐

Metrics

本文评价