一种以H2S为燃料的固体氧化物燃料电池

华南理工大学学报(自然科学版) ›› 2004, Vol. 32 ›› Issue (3): 1-4.

• • 下一篇

一种以H₂S为燃料的固体氧化物燃料电池

陈建军¹ 钟理¹ 韦国林² Karl Chuang²

1．华南理工大学化工学院广东广州510640；2．阿伯塔大学化学与材料工程系加拿大艾特蒙顿 AB T⁶G²G⁶

收稿日期:2002-09-09 出版日期:2004-03-20 发布日期:2015-09-08
通信作者: 陈建军（1965－）男副教授博士生主要从事环境工程与化学工艺研究． E-mail:celzhong＠scut.edu.cn
作者简介:陈建军（1965－）男副教授博士生主要从事环境工程与化学工艺研究．
基金资助:
广东省自然科学基金资助项目（031424）

A Solid Oxide Fuel Cell with H₂S as the Fuel

Chen Jian-jun¹ Zhong Li¹ Wei Guo-lin² Karl Chuang²

1．College of Chemical EngineeringSouth China Univ．of Tech．Guangzhou510640GuangdongChina；
2．Dept．of Chemical and Materials EngineeringUniv．of AlbertaEdmonton AB T⁶G²G⁶Canada

Received:2002-09-09 Online:2004-03-20 Published:2015-09-08
Contact: Chen Jian-jun （born in 1965）maleasso-ciate professorPh．D．candidatemainly researches on environmental engineering and chemical technology． E-mail:celzhong＠scut.edu.cn
About author:Chen Jian-jun （born in 1965）maleasso-ciate professorPh．D．candidatemainly researches on environmental engineering and chemical technology．
Supported by:
Supported by Guangdong Provincial Natural Science Foundation （031424）

摘要/Abstract

摘要： 研究了在一个大气压和750～850℃下具有 H 2 S、（MoS 2 ＋NiS＋Ag）／YSZ／Pt 和空气结构的固体氧化物燃料电池的电化学性能发现升温有助于增强电解质的离子传导性使电池性能变好．在750℃下阳极通入 H 2 S、阴极通入空气时电池的最大电流密度和最大功率密度分别达800mA／cm2 和84mW／cm 2 ；在850℃下电池的最大电流密度和功率密度分别达1750mA／cm2 和200mW／cm 2 ．

关键词: 固体氧化物燃料电池, 硫化氢, H 2 S／O 2 燃料电池, 电池性能

Abstract: The electrochemical performance of a solid oxide fuel cell with the configuration of H 2 S（MoS 2 ＋NiS＋Ag）／YSZ／Pt and air was examined at an atmospheric pressure and 750～850℃．It is found that the increasing of temperature helps to enhance the ionic conductivity of electrolyte and makes the cell performance better．When the H 2 S stream flows into the anode and air stream into the cathodethe maximum electric current density and the maximum power density go respectively up to 800mA／cm 2 and84mW／cm 2 at750℃while those at850℃ respectively to1750mA／cm 2 and200mW／cm 2.

Key words: solid oxide fuel cell, hydrogen sulfide, H₂S／O₂ fuel cell, cell performance

中图分类号:

TM911.4

陈建军, 钟理, 韦国林, 等. 一种以H₂S为燃料的固体氧化物燃料电池[J]. 华南理工大学学报(自然科学版), 2004, 32(3): 1-4.

Chen Jian-jun, Zhong Li, Wei Guo-lin, et al. A Solid Oxide Fuel Cell with H₂S as the Fuel[J]. Journal of South China University of Technology(Natural Science Edition), 2004, 32(3): 1-4.

[1]	钟理 Chuang Karl. H₂S含量及流量对燃料电池性能的影响[J]. 华南理工大学学报（自然科学版）, 2009, 37(9): 123-127.
[2]	隋静唐玉宝刘江. 过渡层对掺Al₂O₃的YSZ电解质支撑SOFC的影响[J]. 华南理工大学学报（自然科学版）, 2008, 36(7): 47-50,56.
[3]	钟理朱斌 Chuang Karl . 复合Li₂SO₄质子传导膜的制备及电化学性能[J]. 华南理工大学学报（自然科学版）, 2008, 36(7): 1-5.
[4]	钟理 Chuang Karl. 纳米复合Li₂ SO₄ 质子传导膜H₂S 中温燃料电池[J]. 华南理工大学学报（自然科学版）, 2007, 35(10): 117-123.
[5]	钟理 Luo Jing Li Chuang Karl. 中温质子传导膜H₂S燃料电池电极催化剂[J]. 华南理工大学学报（自然科学版）, 2006, 34(10): 1-5.
[6]	董新法简弃非王毓娟林维明. 甲烷完全氧化反应的Cu/Ce-Zr-O固溶体电催化剂[J]. 华南理工大学学报（自然科学版）, 2005, 33(11): 22-25,36.

一种以H₂S为燃料的固体氧化物燃料电池

A Solid Oxide Fuel Cell with H₂S as the Fuel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 6

编辑推荐

Metrics

本文评价